• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.3.2016.tde-07072016-152302
Documento
Autor
Nombre completo
Franco Alves Lavacchini Ramunno
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2015
Director
Tribunal
Tenório, Jorge Alberto Soares (Presidente)
Bernardes, Andrea Moura
Espinosa, Denise Crocce Romano
Título en portugués
Estudo cinético da lixiviação de metais de placas de circuito impresso obsoletas.
Palabras clave en portugués
Cinética
Lixiviação
Placas de circuito impresso
Resíduos (Reciclagem)
Resumen en portugués
O processo tradicional de recuperação de metais de resíduos de equipamentos eletroeletrônicos (REEE) geralmente envolve processamento pirometalúrgico. Entretanto, o uso desta tecnologia para processar placas de circuito impresso (PCI) obsoletas pode levar à liberação de dioxinas e furanos, devido à decomposição térmica de retardantes de chama e resinas poliméricas presentes no substrato das placas. Portanto, este trabalho propõe uma rota hidrometalúrgica para recuperação de metais. O comportamento dos metais, com destaque para cobre, zinco e níquel, durante a lixiviação ácida, foi estudado em três temperaturas diferentes (35ºC, 65ºC e 75ºC), com e sem adição de um agente oxidante (peróxido de hidrogênio H2O2). A cinética de dissolução ácida desses metais foi estudada baseada na análise química por ICP-OES (Espectrometria de emissão ótica por plasma acoplado indutivamente) e EDX (Espectroscopia de fluorescência de raios-X por energia dispersiva). O balanço de massa e a análise química indicaram que a etapa de lixiviação sem adição de oxidante é pouco eficaz na extração dos metais, sendo responsável pela dissolução de menos do que 6% do total extraído. A 65ºC e H2SO4 1 mol/L, com adição de 5 mL de H2O2 (30%) a cada quinze minutos e densidade de polpa de 1 g / 10 mL, 98,1% do cobre, 99,9% do zinco e 99,0% do níquel foram extraídos após 4 horas. A cinética de dissolução desses metais é controlada pela etapa da reação química, seguindo, dependendo da temperatura, a equação 1 (1 XB)1/3 = k1.t ou a equação ln (1 XB) = k4.t.
Título en inglés
Kinetic study on leaching of metals from waste printed circuit boards.
Palabras clave en inglés
Kinetics
Leaching
Printed circuit boards
Resumen en inglés
The traditional process for recovery of metals from waste electric and electronic equipment (WEEE) usually involves pyrometallurgical processing. However, the application of this technology to processing waste printed circuit boards (WPCBs) might lead to the formation of dioxins and furans, due to thermal degradation of flameretardants and polymeric resins present in the board substrate. Therefore, this work proposes a hydrometallurgical route for the recovery of metals. The acid leaching behavior of metals, especially copper, zinc and nickel, has been investigated at three different temperatures (35ºC, 65ºC e 75ºC) with and without the addition of an oxidizing agent (hydrogen peroxide H2O2). The dissolution kinetics for acid leaching of these metals was studied based on chemical analysis by ICP-OES (Inductively Coupled Plasma - Optical Emission Spectrometry) and EDX (Energy Dispersive X-ray Spectroscopy). The mass balance and chemical analysis showed that the acid leaching without the addition of an oxidizing agent is inefficient at extracting the metals, being responsible for less than 6% of the total mass leached during the hydrometallurgical route proposed. At 65ºC with 1 mol/L H2SO4 added 5 mL H2O2 (30%) each fifteen minutes under pulp density of 1 g / 10 mL, 98,1% of copper, 99,9% of zinc and 99,0% of nickel were extracted after 4 hours. The dissolution kinetics of these metals, depending on the temperature, followed 1 (1 XB)1/3 = k1.t or ln (1 XB) = k4.t, i.e. chemically controlled reaction model.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-07-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.