Tesis Doctoral
DOI
https://doi.org/10.11606/T.3.2008.tde-06042009-180516
Documento
Autor
Nombre completo
Márcia Rodrigues de Morais Chaves
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Büchler, Pedro Maurício (Presidente)
Dockal, Edward Ralph
Dweck, Jo
Pereira Filho, Edenir Rodrigues
Valenzuela Díaz, Francisco Rolando
 
Título en portugués
Preparação de sílica organofuncionalizada a partir de casca de arroz, com capacidade adsorvente de íons metálicos.
Palabras clave en portugués
Cádmio
Metais
Química de superfície
Resumen en portugués
Esta tese apresenta a obtenção de sílica xerogel a partir de carvão de cascas de arroz e a modificação da sua superfície com um ligante orgânico tipo base de Schiff. O objetivo da utilização deste resíduo agroindustrial é a obtenção de um adsorvente capaz de atuar no tratamento de águas contaminadas contendo íons cádmio II, em uma concepção de valorização de resíduos. A sílica contida na biomassa foi obtida na forma de silicato de sódio através de extração química com solução de hidróxido de sódio, seguida de hidrólise e condensação do monômero através do processo solgel. A modificação da superfície da sílica com o ligante salen foi realizada utilizando o 1,2-dicloroetano como espaçador bifuncional. A sílica xerogel modificada foi avaliada através de análises de isotermas de adsorção e dessorção de nitrogênio (BET/BJH), difração de raios-X (DRX), análise química elementar (CHN), espectroscopia de infravermelho com transformada de Fourier (FTIR), microscopia eletrônica de varredura (MEV) e termogravimetria (TG/DTG). A análise elementar indicou que 0,341 mmol/g de 1,2-dicloroetano e 0,095 mmol/g de salen foi ancorado na superfície da sílica, que apresentou estabilidade térmica até 209°C e área de superfície específica de 106,4 m²/g. Foi realizado um estudo sobre a capacidade de adsorção de íons cádmio (II) pela sílica modificada e não modificada. Os resultados indicam a superior capacidade de adsorção de cádmio pela sílica modificada, em soluções com baixa concentração do íon.
 
Título en inglés
Preparation of organically modified silica from rice husk with capacity to sorption of metallic ions.
Palabras clave en inglés
Adsorbent
Adsorption
Organically modified silica
Rice husk
Schiff-base
Xerogel silica
Resumen en inglés
This thesis presents the obtainment of silica xerogel by rice husk charcoal and its surface modification using an organic ligand type Schiff-base. The purpose of this agro-industrial residue utilization is the production of an adsorbent capable to remove heavy metals present in contaminated waters. The silica contained in the biomass was obtained by alkaline extraction in sodium silicate with hydrolysis through sol-gel process, and modified with salen, using 1,2-dichloroethane as bi-functional spacer. The modified xerogel silica was evaluated through analysis of nitrogen adsorption/desorption isotherms (BET/BJH), X-ray diffraction (XRD), chemical elementary analysis (CHN), Fourier transform infrared spectroscopy (FTIR), scanning electronic microscopy (SEM) and thermogravimetric analysis (TG/DTG). The elementary analysis pointed that 0,341mmol/g of the 1,2-dichloroethane and 0,095mmol/g of the salen was anchored to the silica surface, that presented thermal stability until 209°C and specific surface area of 106,4 m²/g. An evaluation about the ion cadmium II adsorption capacity of the silica modified and unmodified was performed. The results pointed to the superior cadmium adsorption capacity for the modified silica if low ion concentration solutions.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
CHAVES_M_R_M.doc (45.50 Kbytes)
Fecha de Publicación
2009-04-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores.
CeTI-SC/STI
© 2001-2024. Biblioteca Digital de Tesis y Disertaciones de la USP.