Disertación de Maestría
DOI
10.11606/D.3.2016.tde-04012016-171021
Documento
Autor
Nombre completo
Caroline Badin
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2015
Director
Tribunal
Giudici, Reinaldo (Presidente)
Sayer, Claudia
Valera, Ticiane Sanches
Título en portugués
Síntese e caracterização de polímero híbrido acrílico-alquídico produzido por polimerização em miniemulsão.
Palabras clave en portugués
Desenho de experimento
Dispersão polimérica
Híbrido acrílico-alquídico
Miniemulsão
Nucleação secundária
Núcleo-casca
Resumen en portugués
Polímeros híbridos são caracterizados por conter numa mesma partícula dois tipos diferentes de polímero, normalmente incompatíveis e ligados por ligações covalentes. Neste trabalho, a síntese de um polímero híbrido acrílico-alquídico pelo processo de miniemulsão foi investigada. Com o objetivo de compreender como diferentes variáveis na fórmula afetam as características físico-químicas finais do látex, um planejamento experimental foi desenhado com o auxílio do software DX9 e os resultados analisados por modelos empíricos de superfície de resposta. Os fatores variados (variáveis independentes) foram: quantidade de co-estabilizante, surfactante e iniciador. Cada um dos fatores contribuiu para a alteração de pelo menos uma característica avaliada, e a sinergia entre eles afeta diretamente o teor de RDG, resposta indicativa do grau de grafitização entre as espécies. O coestabilizante contribuiu para o aumento do diâmetro médio de gotas e da polidispersidade de tamanho de partículas, enquanto reduziu a dureza do filme. A concentração de surfactante alterou o número de partículas por litro, reduzindo o diâmetro médio de partículas e aumentando a polidispersidade. O iniciador aumentou a conversão monomérica. Todas as dispersões de polímero híbrido produzidas apresentaram redução do tamanho médio de gotas para partículas, indicando evidência de nucleação secundária. As avaliações por microscopia eletrônica de transmissão (TEM) e microscopia de força atômica (AFM) mostraram que a morfologia obtida é do tipo núcleo-casca.
Título en inglés
Synthesis and characterization of alkyd-acrylic hybrid polymer produced by miniemulsion polymerization.
Palabras clave en inglés
Alkyd-acrylic hybrid
Core-shell
Design of experiment
Miniemulsion
Polymer dispersion
Secondary nucleation
Resumen en inglés
Hybrid polymers are defined by the presence of two or more different kinds of polymers in the same particle, typically incompatible and linked by covalent bonds. In this work, the synthesis of an alkyd-acrylic hybrid polymer produced by miniemulsion polymerization has been investigated. With the goal of understanding how different variables in the recipe affect the final characteristics of the latex, a design of experiment was planned using DX9 software and the results were analyzed by response surface methodology. The factors studied (independent variables) were: amount of co-stabilizer, surfactant and initiator. Each of these factors contributed to change at least one of the evaluated characteristics, and the synergy between them directly affects the RDG content, response of the polymer degree of grafting. Costabilizer contributed to increase the average droplets diameter and polydispersity of particle size, while reducing the film hardness. The amount of surfactant changed the number of particles, reducing the average particle size and increasing polydispersity. Initiator increased the monomer conversion. All hybrids dispersions presented a decrease in the droplet size to particle size, indicating evidence of secondary nucleation. Core-shell morphology was observed through transmission electron microscopy (TEM) and atomic force microscopy (AFM).
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Catalogacao.pdf (4.95 Kbytes)
Dissert_Caroline.pdf (2.62 Mbytes)
Fecha de Publicación
2016-01-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.