Tese de Doutorado
DOI
https://doi.org/10.11606/T.3.2016.tde-23062016-074259
Documento
Autor
Nome completo
Rafael Guimarães Savioli
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2016
Orientador
Banca examinadora
Ruggieri, Claudio (Presidente)
Andrade, Arnaldo Homobono Paes de
Bianchi, Kleber Eduardo
Burgos, Diego Felipe Sarzosa
Miranda, Carlos Alexandre de Jesus
Título em português
Estudo experimental do comportamento à fratura frágil em aços estruturais ferríticos e aplicações à determinação da curva mestra.
Palavras-chave em português
Aço ASTM A285 Gr C
Aço ASTM A515 Gr 60
Aço inoxidável ferrítico
Curva mestra
Mecânica da fratura
Tenacidade dos materiais
Transição dúctil-frágil
Resumo em português
Este trabalho apresenta uma investigação experimental sobre o comportamento à fratura frágil de aços estruturais ferríticos, ASTM A285 Gr C e ASTM A515 Gr 65. Os resultados deste trabalho ampliam a base de dados de propriedades mecânicas utilizadas nas análises de integridade de estruturas pressurizadas tais como vasos de pressão e tanques de armazenamento construídos com esta classe de material. O trabalho tem por objetivo também avaliar a aplicabilidade de corpos de prova de dimensões reduzidas, PCVN, na determinação da temperatura de referência, T0, por meio da metodologia da Curva Mestra, a qual define a dependência da tenacidade à fratura do material em função da temperatura. Os ensaios de tenacidade à fratura foram conduzidos utilizando-se corpos de prova solicitados em flexão três pontos com geometria SE(B), PCVN e PCVN com entalhe lateral, extraídos de chapas laminadas. Os resultados dos ensaios foram obtidos em termos de integral J no momento da instabilidade, denotados por Jc. Dados adicionais de resistência à tração e de Impacto Charpy convencional também foram obtidos para caracterizar o comportamento mecânico dos aços utilizados. Os resultados mostraram uma forte influência da geometria dos corpos de prova sobre os valores de Jc, evidenciada pela grande variação nos valores de tenacidade à fratura.
Título em inglês
Experimental study on the cleavage fracture behavior of structural ferritic steels and applications to determine the master curve.
Palavras-chave em inglês
ASTM A285 Gr C steel
ASTM A515 Gr 60 steel
Ductile-to-brittle transition
Fracture toughness
Master curve
Resumo em inglês
This work presents an experimental investigation on the cleavage fracture behavior of structural ferritic steels, ASTM A285 Grade C and ASTM A515 Grade 65. One purpose of this study is to enlarge a previously reported work on mechanical and fracture properties for this class of steel to provide a more definite database for use in structural and defect analyses of pressurized components, including pressure vessels and storage tanks. Another purpose is to address the applicability of Precracked V-notch Charpy specimens to determine the reference temperature, T0, derived from the Master Curve Methodology which defines the dependence of fracture toughness with temperature for the tested material. Fracture toughness testing conducted on single edge bend specimens in three-point loading (SE(B), PCVN Plain Side and PCVN Side Grooved) extracted from laminated plates provides the cleavage fracture resistance data in terms of the J-integral at cleavage instability, Jc. Additional tensile and conventional Charpy tests produce further experimental data which serve to characterize the mechanical behavior of the tested materials. The results reveal a strong effect of specimen geometry on Jc values associated with large scatter in the measured values of cleavage fracture toughness.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2016-06-23
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2024. Todos os direitos reservados.