Tesis Doctoral
DOI
https://doi.org/10.11606/T.3.2016.tde-23062016-074259
Documento
Autor
Nombre completo
Rafael Guimarães Savioli
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2016
Director
Tribunal
Ruggieri, Claudio (Presidente)
Andrade, Arnaldo Homobono Paes de
Bianchi, Kleber Eduardo
Burgos, Diego Felipe Sarzosa
Miranda, Carlos Alexandre de Jesus
Título en portugués
Estudo experimental do comportamento à fratura frágil em aços estruturais ferríticos e aplicações à determinação da curva mestra.
Palabras clave en portugués
Aço ASTM A285 Gr C
Aço ASTM A515 Gr 60
Aço inoxidável ferrítico
Curva mestra
Mecânica da fratura
Tenacidade dos materiais
Transição dúctil-frágil
Resumen en portugués
Este trabalho apresenta uma investigação experimental sobre o comportamento à fratura frágil de aços estruturais ferríticos, ASTM A285 Gr C e ASTM A515 Gr 65. Os resultados deste trabalho ampliam a base de dados de propriedades mecânicas utilizadas nas análises de integridade de estruturas pressurizadas tais como vasos de pressão e tanques de armazenamento construídos com esta classe de material. O trabalho tem por objetivo também avaliar a aplicabilidade de corpos de prova de dimensões reduzidas, PCVN, na determinação da temperatura de referência, T0, por meio da metodologia da Curva Mestra, a qual define a dependência da tenacidade à fratura do material em função da temperatura. Os ensaios de tenacidade à fratura foram conduzidos utilizando-se corpos de prova solicitados em flexão três pontos com geometria SE(B), PCVN e PCVN com entalhe lateral, extraídos de chapas laminadas. Os resultados dos ensaios foram obtidos em termos de integral J no momento da instabilidade, denotados por Jc. Dados adicionais de resistência à tração e de Impacto Charpy convencional também foram obtidos para caracterizar o comportamento mecânico dos aços utilizados. Os resultados mostraram uma forte influência da geometria dos corpos de prova sobre os valores de Jc, evidenciada pela grande variação nos valores de tenacidade à fratura.
Título en inglés
Experimental study on the cleavage fracture behavior of structural ferritic steels and applications to determine the master curve.
Palabras clave en inglés
ASTM A285 Gr C steel
ASTM A515 Gr 60 steel
Ductile-to-brittle transition
Fracture toughness
Master curve
Resumen en inglés
This work presents an experimental investigation on the cleavage fracture behavior of structural ferritic steels, ASTM A285 Grade C and ASTM A515 Grade 65. One purpose of this study is to enlarge a previously reported work on mechanical and fracture properties for this class of steel to provide a more definite database for use in structural and defect analyses of pressurized components, including pressure vessels and storage tanks. Another purpose is to address the applicability of Precracked V-notch Charpy specimens to determine the reference temperature, T0, derived from the Master Curve Methodology which defines the dependence of fracture toughness with temperature for the tested material. Fracture toughness testing conducted on single edge bend specimens in three-point loading (SE(B), PCVN Plain Side and PCVN Side Grooved) extracted from laminated plates provides the cleavage fracture resistance data in terms of the J-integral at cleavage instability, Jc. Additional tensile and conventional Charpy tests produce further experimental data which serve to characterize the mechanical behavior of the tested materials. The results reveal a strong effect of specimen geometry on Jc values associated with large scatter in the measured values of cleavage fracture toughness.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-06-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.