Mémoire de Maîtrise
DOI
10.11606/D.3.2007.tde-31032008-095727
Document
Auteur
Nom complet
Tarita Shiraishi Furlan
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2007
Directeur
Jury
Tschiptschin, André Paulo (Président)
Fuoco, Ricardo
Goldenstein, Hélio
Titre en portugais
Influência do teor de estrôncio na modificação da liga A356.
Mots-clés en portugais
Modificação de ligas de alumínio
Resumé en portugais
O objetivo deste trabalho foi o de otimizar a adição de estrôncio em liga A356 visando obter as melhores propriedades mecânicas de ductilidade. Foram estudados diferentes níveis de adição de estrôncio em ligas A356 com dois níveis de fósforo residual. Além disto, foi estudado o efeito de adições crescentes de magnésio na morfologia do silício em liga Al-7%Si modificada. Para a realização deste estudo, foram produzidos corpos de prova de tração segundo ASTM B108 com velocidade de resfriamento de 8°C/s. Os corpos de prova foram endurecidos por precipitação via tratamento térmico e tracionados. Além de uma avaliação quantitativa das propriedades mecânicas, amostras de todas as condições passaram por uma avaliação metalográfica qualitativa. Foi feito também ataque profundo para observação das morfologias das partículas de silício em microscópio eletrônico. O efeito da adição crescente de estrôncio na liga A356 em um intervalo de 0 a 256 ppm de estrôncio foi o de aumento do alongamento até teores de 50 a 60 ppm, seguido de uma diminuição do mesmo até 256 ppm. O teste de adição crescente de estrôncio foi repetido para uma liga A356 com teor residual de fósforo de aproximadamente 10 ppm. A curva de alongamento segue o mesmo formato da curva levantada para amostras que não continham fósforo, embora tenha sido encontrada uma sensível queda nos valores de alongamento na presença de fósforo. A presença de magnésio em ligas Al-Si modificadas por estrôncio foi responsável por uma mudança na morfologia de crescimento das partículas de silício nas regiões de contornos de células eutéticas, além do aparecimento de partículas intermetálicas nesta mesma região. Deste trabalho, concluiu-se que as melhores propriedades mecânicas de ductilidade foram obtidas para a adição de estrôncio de 50 a 60 ppm.
Titre en anglais
Influence of strontium content on the modification of A356 alloy.
Mots-clés en anglais
Aluminum alloys
Magnesium
Modification
Phosphorous
Strontium
Resumé en anglais
This work has, as its main objective, the optimization of the strontium addition in A356 alloy, in order to obtain the best ductility results. The addition of several different strontium amounts in alloys containing two phosphorous amounts was studied. Besides, the effect of increasing magnesium content on the morphology of the silicon particles of Al-7%Si modified alloy was also studied. Test bars were produced from ASTM B108 cooled at a rate of 8°C/s. The samples were heat treated and then tested. The mechanical properties were evaluated and the microstructures were analyzed. The silicon morphology was observed in deep etched samples at SEM. Strontium additions of 0 to 256 ppm increased the elongation up to 50-60 ppm. Above 75 ppm, the addition of strontium caused the elongation to decrease up to 256 ppm. The same test was reproduced for an alloy containing approximately 10 ppm P and, although the best results were achieved at strontium additions of 50-60 ppm, the elongation results were clearly lower. The presence of magnesium in Al-7%Si modified alloys was responsible for a change in the growth morphology of the silicon particles, especially near grain boundaries, and also for the formation of intermetallic particles in those areas. From this work, it was possible to conclude that the best ductility properties are achieved for strontium additions of 50-60 ppm.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
MestradoTarita_rev.pdf (24.21 Mbytes)
Date de Publication
2008-04-07
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.