Disertación de Maestría
DOI
10.11606/D.3.2007.tde-31032008-095727
Documento
Autor
Nombre completo
Tarita Shiraishi Furlan
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2007
Director
Tribunal
Tschiptschin, André Paulo (Presidente)
Fuoco, Ricardo
Goldenstein, Hélio
Título en portugués
Influência do teor de estrôncio na modificação da liga A356.
Palabras clave en portugués
Modificação de ligas de alumínio
Resumen en portugués
O objetivo deste trabalho foi o de otimizar a adição de estrôncio em liga A356 visando obter as melhores propriedades mecânicas de ductilidade. Foram estudados diferentes níveis de adição de estrôncio em ligas A356 com dois níveis de fósforo residual. Além disto, foi estudado o efeito de adições crescentes de magnésio na morfologia do silício em liga Al-7%Si modificada. Para a realização deste estudo, foram produzidos corpos de prova de tração segundo ASTM B108 com velocidade de resfriamento de 8°C/s. Os corpos de prova foram endurecidos por precipitação via tratamento térmico e tracionados. Além de uma avaliação quantitativa das propriedades mecânicas, amostras de todas as condições passaram por uma avaliação metalográfica qualitativa. Foi feito também ataque profundo para observação das morfologias das partículas de silício em microscópio eletrônico. O efeito da adição crescente de estrôncio na liga A356 em um intervalo de 0 a 256 ppm de estrôncio foi o de aumento do alongamento até teores de 50 a 60 ppm, seguido de uma diminuição do mesmo até 256 ppm. O teste de adição crescente de estrôncio foi repetido para uma liga A356 com teor residual de fósforo de aproximadamente 10 ppm. A curva de alongamento segue o mesmo formato da curva levantada para amostras que não continham fósforo, embora tenha sido encontrada uma sensível queda nos valores de alongamento na presença de fósforo. A presença de magnésio em ligas Al-Si modificadas por estrôncio foi responsável por uma mudança na morfologia de crescimento das partículas de silício nas regiões de contornos de células eutéticas, além do aparecimento de partículas intermetálicas nesta mesma região. Deste trabalho, concluiu-se que as melhores propriedades mecânicas de ductilidade foram obtidas para a adição de estrôncio de 50 a 60 ppm.
Título en inglés
Influence of strontium content on the modification of A356 alloy.
Palabras clave en inglés
Aluminum alloys
Magnesium
Modification
Phosphorous
Strontium
Resumen en inglés
This work has, as its main objective, the optimization of the strontium addition in A356 alloy, in order to obtain the best ductility results. The addition of several different strontium amounts in alloys containing two phosphorous amounts was studied. Besides, the effect of increasing magnesium content on the morphology of the silicon particles of Al-7%Si modified alloy was also studied. Test bars were produced from ASTM B108 cooled at a rate of 8°C/s. The samples were heat treated and then tested. The mechanical properties were evaluated and the microstructures were analyzed. The silicon morphology was observed in deep etched samples at SEM. Strontium additions of 0 to 256 ppm increased the elongation up to 50-60 ppm. Above 75 ppm, the addition of strontium caused the elongation to decrease up to 256 ppm. The same test was reproduced for an alloy containing approximately 10 ppm P and, although the best results were achieved at strontium additions of 50-60 ppm, the elongation results were clearly lower. The presence of magnesium in Al-7%Si modified alloys was responsible for a change in the growth morphology of the silicon particles, especially near grain boundaries, and also for the formation of intermetallic particles in those areas. From this work, it was possible to conclude that the best ductility properties are achieved for strontium additions of 50-60 ppm.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
MestradoTarita_rev.pdf (24.21 Mbytes)
Fecha de Publicación
2008-04-07
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.