Master's Dissertation
DOI
10.11606/D.3.2007.tde-31032008-095727
Document
Author
Full name
Tarita Shiraishi Furlan
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2007
Supervisor
Committee
Tschiptschin, André Paulo (President)
Fuoco, Ricardo
Goldenstein, Hélio
Title in Portuguese
Influência do teor de estrôncio na modificação da liga A356.
Keywords in Portuguese
Modificação de ligas de alumínio
Abstract in Portuguese
O objetivo deste trabalho foi o de otimizar a adição de estrôncio em liga A356 visando obter as melhores propriedades mecânicas de ductilidade. Foram estudados diferentes níveis de adição de estrôncio em ligas A356 com dois níveis de fósforo residual. Além disto, foi estudado o efeito de adições crescentes de magnésio na morfologia do silício em liga Al-7%Si modificada. Para a realização deste estudo, foram produzidos corpos de prova de tração segundo ASTM B108 com velocidade de resfriamento de 8°C/s. Os corpos de prova foram endurecidos por precipitação via tratamento térmico e tracionados. Além de uma avaliação quantitativa das propriedades mecânicas, amostras de todas as condições passaram por uma avaliação metalográfica qualitativa. Foi feito também ataque profundo para observação das morfologias das partículas de silício em microscópio eletrônico. O efeito da adição crescente de estrôncio na liga A356 em um intervalo de 0 a 256 ppm de estrôncio foi o de aumento do alongamento até teores de 50 a 60 ppm, seguido de uma diminuição do mesmo até 256 ppm. O teste de adição crescente de estrôncio foi repetido para uma liga A356 com teor residual de fósforo de aproximadamente 10 ppm. A curva de alongamento segue o mesmo formato da curva levantada para amostras que não continham fósforo, embora tenha sido encontrada uma sensível queda nos valores de alongamento na presença de fósforo. A presença de magnésio em ligas Al-Si modificadas por estrôncio foi responsável por uma mudança na morfologia de crescimento das partículas de silício nas regiões de contornos de células eutéticas, além do aparecimento de partículas intermetálicas nesta mesma região. Deste trabalho, concluiu-se que as melhores propriedades mecânicas de ductilidade foram obtidas para a adição de estrôncio de 50 a 60 ppm.
Title in English
Influence of strontium content on the modification of A356 alloy.
Keywords in English
Aluminum alloys
Magnesium
Modification
Phosphorous
Strontium
Abstract in English
This work has, as its main objective, the optimization of the strontium addition in A356 alloy, in order to obtain the best ductility results. The addition of several different strontium amounts in alloys containing two phosphorous amounts was studied. Besides, the effect of increasing magnesium content on the morphology of the silicon particles of Al-7%Si modified alloy was also studied. Test bars were produced from ASTM B108 cooled at a rate of 8°C/s. The samples were heat treated and then tested. The mechanical properties were evaluated and the microstructures were analyzed. The silicon morphology was observed in deep etched samples at SEM. Strontium additions of 0 to 256 ppm increased the elongation up to 50-60 ppm. Above 75 ppm, the addition of strontium caused the elongation to decrease up to 256 ppm. The same test was reproduced for an alloy containing approximately 10 ppm P and, although the best results were achieved at strontium additions of 50-60 ppm, the elongation results were clearly lower. The presence of magnesium in Al-7%Si modified alloys was responsible for a change in the growth morphology of the silicon particles, especially near grain boundaries, and also for the formation of intermetallic particles in those areas. From this work, it was possible to conclude that the best ductility properties are achieved for strontium additions of 50-60 ppm.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
MestradoTarita_rev.pdf (24.21 Mbytes)
Publishing Date
2008-04-07
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2022. All rights reserved.