Disertación de Maestría
DOI
10.11606/D.3.2008.tde-30052008-130528
Documento
Autor
Nombre completo
Thiago Capeletti
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Brandi, Sérgio Duarte (Presidente)
Azevedo, Cesar Roberto de Farias
Souza, Paulo Cezar Rioli Duarte de
Título en portugués
Estudo da brasabilidade de contatos elétricos por metal de adição 40%Ag-21%Zn-20%Cd-19%Cu.
Palabras clave en portugués
Brasabilidade
Contatos elétricos
Prata-óxido de estanho
Resumen en portugués
Contatos elétricos são aplicados na área de geração, manuseio e distribuição de energia elétrica, sendo fabricados em metais condutores como: cobre eletrolítico e suas ligas. Através de alguns métodos de brasagem, pastilhas com propriedades de condutividade, elétrica e térmica, mais apuradas são brasadas sobre estas bases condutoras. Em função da substituição do cádmio por um elemento menos nocivo ao homem e ao meio ambiente, o estanho vem se difundindo com rapidez, apoiado por iniciativas internacionais. O objetivo deste trabalho é avaliar a brasabilidade de um metal de adição na liga 40%Ag-21%Zn- 20%Cd-19%Cu, sobre metais de base em: cobre eletrolítico, latão (65%Cu-35%Zn), prata pura e prata-óxido de estanho (90%Ag-10%SnO2) através dos ensaios da gota séssil e da cunha. As amostras foram caracterizadas metalograficamente. Os resultados mostraram que a brasabilidade para todos os substratos empregados estava dentro de valores de ângulo de contato menores que 10o, com exceção do substrato prata-óxido de estanho. Para este material ocorreu o demolhamento, dificultando a caracterização da sua molhabilidade.
Título en inglés
Investigation of electrical contacts brazeability by filler metal 40%Ag-21%Zn-20%Cd-19%Cu.
Palabras clave en inglés
Brazeability
Electrical contacts
Silver-tin oxide
Resumen en inglés
Electrical contacts are manufactured with conductive metals, like electrolytic copper and its alloys. These products are used in electric circuits to manage the electrical energy. Electrical contacts assemblies can be built up by brazing joining methods, which improves electrical and thermal conductivity in non-ferrous substrates. The cadmium oxide, present into electrical contact alloys, has been replaced by tin oxide due to environmental issues, to meet the actual internationals agreements. The objective of this work is to evaluate the brazeability of a filler metal 40%Ag-21%Zn-20%Cd-19%Cu, on non-ferrous substrates, like: electrolytic copper, brass (65%Cu-35%Zn), silver and silver tin-oxide (90%Ag- 10%SnO2) using sessile drop and edge tests. The results showed that the brazeability of all non-ferrous substrates depicted contact angles less than 10º, except for the silver-tin oxide substrate. For silver-tin oxide substrate dewetting took place and the measurement of contact angles was impossible.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-07-02
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.