Disertación de Maestría
DOI
10.11606/D.3.2009.tde-29062009-103030
Documento
Autor
Nombre completo
Olmede Celestino dos Santos Filho
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Schön, Cláudio Geraldo (Presidente)
Lima, Nelson Batista de
Padilha, Angelo Fernando
Título en portugués
Caracterizações de propriedades microestruturais e mecânicas de ligas AA 1100 e AA 5052 processadas pela técnica de laminação acumulativa ("Accumulated Roll Bonding - ARB").
Palabras clave en portugués
Conformação mecânica
Metalurgia física
Textura
Resumen en portugués
Nesta dissertação de mestrado foram utilizadas duas ligas de alumínio (AA1100 e AA5052) para a produção de uma microestrutura final apresentando tamanho médio de grãos menores que um micrometro. Tal fato foi possível através do processo de Accumulated Roll Bonding (ARB). Tais materiais produzidos por ARB, foram caracterizados conforme propriedades mecânicas (microdureza, limite de escoamento e resistência) e microestruturais (tamanho de grão e macrotextura e composição química dos precipitados). O principal resultado para este trabalho foi a produção de tiras de AA 1100 e AA 5052 com tamanho médio de grão de 0,50 ± 0,04 m e 0,42 ± 0,06 m respectivamente. Tal resultado é coerente em comparação à literatura. Com relação aos resultados de textura, tais amostras apresentaram temperatura de recristalização acima de 473K e componente de textura típicas de cisalhamento (tanto para o material oriundo de fábrica como para o material laminado). Tal fato é esperado já que não se utilizou lubrificação durante ensaios de laminação. A propriedade mecânica de microdureza de AA 1100 ficou coerente com a literatura embora as propriedades de limite de escoamento e de resistência possuíram módulos abaixo da literatura.
Título en inglés
Characterization of microestrutural and mechanical properties from AA1100 and AA5052 alloys that were processed by Accumulated Roll Bonding - ARB.
Palabras clave en inglés
AA1100
AA5052
Accumulates Roll Bonding
ARB
Grain refining
Mechanical working
Nanograins
Strip rolling
Texture
Ultra-fine grains
Resumen en inglés
The present work is related to the production, in a laboratory scale, of a metallic microstructure having a grain size smaller than one micrometer, through the Accumulated Roll Bonding technique(ARB), for two different aluminum alloys, namely AA 1100 and AA 5052. The strips obtained by the ARB technique have been characterized by their mechanical properties (microhardness, yield and tensile strength), and their microstructure (grain size, macrotexture and precipitates chemical composition). The main result of this work has been the rolling of AA1100 and AA5052 strips with an average grain size of 0.5 ± 0.04 m and 0.42 ± 0.06 m respectively. Such results are consistent with the literature. Relative to the texture, the samples presented a recrystallization temperature higher than 473K and typical shear texture components (due to the dry rolling conditions during the ARB). Microhardness of the AA110 was consistent with literature data; however yield and tensile strength presented values that were lower than those observed in the literature.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
MESTRADO_OLMEDE.pdf (7.83 Mbytes)
Fecha de Publicación
2009-10-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.