• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Mémoire de Maîtrise
DOI
10.11606/D.3.1997.tde-27072001-165148
Document
Auteur
Nom complet
Antonio José Ramirez Londoño
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 1997
Directeur
Jury
Brandi, Sergio Duarte (Président)
Pope, Alexandre Meirelles
Taniguchi, Celio
Titre en portugais
Estudo da precipitação de nitreto de cromo e fase sigma por simulação térmica da zona afetada pelo calor na soldagem multipasse de aços inoxidáveis duplex.
Mots-clés en portugais
fase sigma
nitreto de cromo
precipitação de fases intermetálicas
soldagem de aços inoxidáveis duplex
Resumé en portugais
Os aços inoxidáveis duplex são materiais com um excelente desempenho, devido às suas sobressalentes propriedades mecânicas e excelente resistência à corrosão. Uma composição química adequada e microestrutura balanceada são as responsáveis por esta combinação de propriedades. No entanto, são estes mesmos fatores que os fazem especialmente susceptíveis à precipitação de fases intermetálicas, com efeitos maléficos no seu desempenho. Durante os ciclos térmicos de uma soldagem multipasse, a precipitação de intermetálicos é crítica. Foi desenvolvido um método para simular os ciclos térmicos de uma solda multipasse. Usando este método, foi estudada a precipitação de nitreto de cromo e fase sigma na zona afetada pelo calor submetida a temperaturas abaixo de 950°C dos aços inoxidáveis duplex UNS S31803 e S32550. Foram estudadas energias de soldagem na faixa de 0,4 a 1,0 kJ/mm. Foi determinada mediante extração de precipitados, seguida de difração de raios X na câmara de Debye-Scherrer e microscopia eletrônica de transmissão, a precipitação de nitreto de cromo para energias de soldagem de 0,4 a 1,0 kJ/mm e de fase sigma para energias de soldagem de 0,6-1,0 KJ/mm, no UNS S32550. Já o UNS S31803 não apresentou precipitação alguma para as energias de soldagem estudadas. Baseando-se nos resultados verifica-se que durante uma soldagem multipasse o UNS S31803 é menos propenso que o UNS S32550 à precipitação de intermetálicos na zona afetada pelo calor submetida a temperaturas abaixo de 950°C.
Titre en anglais
Chromium nitride and sigma phase precipitation study by heat-affected zone thermal simulation of duplex stainless steels multipass welding.
Mots-clés en anglais
chromium nitride
duplex stainless steels welding
intermetallic phases precipitation
sigma phase
Resumé en anglais
Duplex stainless steels belong to a group of high performance stainless steels regarding to corrosion and mechanical properties. These achievements are related to a suitable chemical composition and a balanced microstructure. During welding thermal cycles the microstructure changes and, consequently, corrosion and mechanical properties might be impaired due to a precipitation of intermetallic phases. This precipitation is an issue to be addressed for multipass welding. It was developed a method for simulate the multipass welding thermal cycles. Using this method chromium nitride and sigma phase precipitation was studied in a simulated heat affected zone of multipass welding (three passes) of UNS S31803 and UNS S32550 duplex stainless steels with different heat inputs (0,4 to 1,0 kJ/mm). The HAZ simulated region was below 950°C maximum temperature. Microstructural characterization of simulated samples showed discontinuous films of a precipitated phase at ferrite/ferrite grain boundaries and ferrite/austenite interfaces were observed only in a UNS S32550 duplex grade for all heat inputs simulated. This suggests that sigma phase and chromium nitride precipitation took place during sample thermocycling. X-ray diffraction in a Debye-Scherrer chamber of extracted precipitates and electron diffraction by TEM confirmed the presence of chromium nitrides for all range of heat input studied and sigma phase for heat input above 0,6 kJ/mm. On the other hand, microstructural analysis of UNS S31803 simulated samples did not present precipitation of intermetallic phases in the tested temperature range of HAZ. Based on these results, UNS S31803 is more resistant than UNS S32550 to intermetallic phases precipitation in multipass welding.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Antonio-Ramirez.pdf (3.52 Mbytes)
Date de Publication
2001-08-14
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.