Master's Dissertation
DOI
10.11606/D.3.2014.tde-26122014-115756
Document
Author
Full name
Márcio Toshio Tanaka
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2014
Supervisor
Committee
Mourão, Marcelo Breda (President)
Ferreira Neto, João Batista
Takano, Cyro
Title in Portuguese
Estudo experimental de briquetes autorredutores e auto-aglomerantes de minério de ferro e carvão fóssil.
Keywords in Portuguese
Alto-forno
Auto-aglomerado
Autorredutor
Briquetagem a frio de minério de ferro e carvão
Briquete compósito de carbono e minério de ferro
Abstract in Portuguese
Este trabalho consiste no estudo da obtenção de aglomerados autorredutores na forma de briquetes a frio tratados termicamente, utilizando minério de ferro e carvão fóssil como matérias-primas. Esta promissora tecnologia tem como premissa a utilização da termo-plasticidade do carvão fóssil para conferir resistência e promover a auto-aglomeração. A obtenção de briquetes dá-se através de três etapas: condicionamento da mistura, briquetagem a frio e tratamento térmico. Os finos de carvão e minério são misturados e homogeneizados. A mistura, então, passa por processo de briquetagem a frio para compactação, promove o aumento de contato entre as partículas de carvão e minério. Finalmente tratamento térmico é realizado para obter a forma de um corpo sólido e coeso de auto-aglomerado autorredutor. O objetivo deste trabalho é determinar as melhores condições de obtenção de briquetes através do estudo de variáveis ao longo do processo de fabricação, utilizando a resistência mecânica como parâmetro. As variáveis estudadas são: granulometria do carvão, envelhecimento do carvão, percentual de carvão na mistura, adição de aglomerantes, pressão de compactação na briquetagem e temperatura de tratamento térmico. Os resultados obtidos neste estudo indicam que estas variáveis afetam significativamente a resistência mecânica. Utilizando-se o carvão Chipanga, o melhor resultado de resistência à compressão foi de 19,82 Mpa. Foram consideradas as seguintes condições de fabricação: mistura na proporção de 75:25 (% em massa) de minério para carvão Chipanga, o carvão continha finos inferiores à 0,075 mm, sem a adição de aglomerantes, e o tratamento térmico foi realizado na temperatura de máxima fluidez do carvão. Além disto, foi observado que as partículas de minério de ferro foram concentradas nas regiões periféricas do briquete após tratamento térmico, e que o envelhecimento do carvão afeta negativamente a propriedade de termo-plasticidade.
Title in English
Experimental study of self-reducing self-agglomerated iron ore and brown coal briquettes.
Keywords in English
Blast furnace
Carbon composite iron ore hot briquette
Coal and iron ore cold briquetting
Self-agglomerated
Self-reduction
Abstract in English
This work is focused in the study of obtaining self-reducing cold briquettes of agglomerates, by using iron ore and coal as raw materials. This promising technology has its foundation on the thermo plasticity of coal to manage high mechanical resistance when it is compared with self-reducing pellets. Three steps mainly describes how to obtaining briquettes: mixture, cold briquetting and heat treatment. Fines of raw material are mixed and cold briquetting process results in a compact mixture. This might lead to closer contact between particles of iron ore and coal. Finally, heat treatment is performed to achieve a cohesive body and solid shape containing self-reducing agglomerated. The main purpose of this job is to comprehend the fundamentals on how to obtain self-reducing cold briquettes of agglomerated carbon and iron, by understanding the background of it variables along the manufacturing process, and using mechanical resistance as reference. The variables list is: the particle size of the coal, coal aging, percentage of coal in the mixture, adding binders, briquetting pressure and temperature of heat treatment. The results of this study indicate that these variables affect significantly the mechanical strength. Using Chipanga coal, the best compressive strength achieved was 19.82 MPa. It was considered the following manufacturing variables: the mixture ratio of 75:25 (wt% of iron ore and coal), fines of coal containing less than 0.075 mm, without binders, and heat treatment was performed at the temperature of coal´s maximum fluidity. Moreover, it was observed that the particles of iron ore were concentrated in the peripheral regions of the briquette after heat treatment, and that coal´s aging negatively affects the property of thermo-plasticity.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2015-01-19
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.