Disertación de Maestría
DOI
10.11606/D.3.2013.tde-26122013-154756
Documento
Autor
Nombre completo
Jaime Casanova Soeiro Junior
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Brandi, Sérgio Duarte (Presidente)
Schön, Cláudio Geraldo
Souza, Paulo Cézar Rioli Duarte de
Título en portugués
Estudo da soldabilidade do tubo API 5L X80 utilizando os processos de soldagem eletrodo revestido e MAG com transferência controlada na raiz e enchimento com arame tubular autoprotegido.
Palabras clave en portugués
Soldagem a arco
Soldagem a gás
Tubos
Resumen en portugués
Na indústria de petróleo e gás as tubulações são formas eficientes de transportar esses produtos ou seus derivados das regiões de exploração para as refinarias e em alguns casos até o consumidor. O principal tipo de aço utilizado na fabricação dessas tubulações são os aços ARBL que devido à boa relação entre resistência à tração e tenacidade a baixas temperaturas geram uma boa relação custo/benefício na utilização e na montagem de tubulações. Neste trabalho é apresentado um estudo sobre a soldabilidade do tubo API 5L X80 construído com aço ARBL. Os corpos-de-prova utilizados foram anéis de 508 mm de diâmetro externo com espessura de parede de 19,0 mm. A soldagem foi executada com o processo eletrodo revestida no experimento 1, em um par de anéis, e o outro par de anéis foi soldado, na raiz, com o processo de soldagem MAG-TC e nos passes de enchimento e acabamento foi utilizado o processo arame tubular auto-protegido. Os resultados dos ensaios de resistência à tração, dobramento lateral e de Nick-Break demonstram que ambos os procedimentos de soldagem são qualificados pela norma API 1104. Associando o resultado do ensaio de Charpy V a 0°C e associando-o a quantificação das frações volumétricas de microconstituintes MA e a caracterização microestrutural é possível observar que os valores de energia absorvida na ZAC tem maior relação com o mecanismo de refino de grão, que melhora os valores obtidos, do que com a quantidade de fração volumétrica do microconstituinte MA.
Título en inglés
Study of weldability of API 5L X80 steel pipe using the welding processes of shielded metal arc welding and GMAW-CT in the root pass and self shielded flux cored in filling and finishing passes.
Palabras clave en inglés
API 5L X80 steel
FCAW
GMAW-CT
Oil and gas industries
Self shielded tubular wire
SMAW
Resumen en inglés
In the oil and gas industries, pipelines are efficient ways of transporting these products, or its derivatives, from exploration regions to refineries and, in some cases, up to the final consumer. The main type of steel used in manufacturing these pipelines are HSLA steels that, due to the good relationship between tensile strength and toughness at low temperatures, create a cost/benefit ratio in the use and installation of these pipelines. This paper presents a study on the weldability of API 5L X80 HSLA pipe steel. The samples used were pipe rings with 508 mm outside diameter and a wall thickness of 19.0 mm. The root welding process was performed using SMAW in Experiment 1 with filing and finishing passes with SMAW. In the second experiment, the root pass were welded with GMAW-CT, and filling and finishing passes with FCAW-SS. Tensile test results, lateral bending tests and 'Nick-Break' tests showed that both welding procedures were qualified according to API 1104 Standard. Associating these results with Charpy V test at 0°C and with quantification of volume fractions of MA microconstituent is possible to observe that the values of absorbed energy in the HAZ are more closely related to the mechanism of grain refinement, which improves the values obtained with the volume fraction of the amount of microconstituent MA.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-01-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.