• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Mémoire de Maîtrise
DOI
Document
Auteur
Nom complet
Raphael Oliveira Ferreira
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2019
Directeur
Jury
Azevedo, Cesar Roberto de Farias (Président)
Machado, Izabel Fernanda
Magnabosco, Rodrigo
Titre en portugais
Caracterização microestrutural de discos metálicos de aço AISI 4140 após ensaios tribológicos do tipo pino-disco, usando pinos de alumí­nio 6082-T6, cobre C10200 e latão C36000.
Mots-clés en portugais
Materiais
Microscopia eletrônica
Tribologia
Resumé en portugais
Foram realizados ensaios tribológicos do tipo pino-disco com pinos de cobre puro, alumínio e latão para sob cargas normais de 10, 20 e 50 N contra discos de aço, que foram analisados após os ensaios utilizando interferometria óptica 3D e microscopia eletrônica de varredura. O par tribológico cobre-aço apresentou curva de coeficiente de atrito instável, com valor médio de 0,65. Os pares alumínio-aço e latão-aço apresentaram curvas de coeficiente de atrito mais estáveis que aquelas apresentadas nos ensaios com pinos de cobre, com valor médio de coeficiente de atrito de 0,42 e 0,30, respectivamente. Tanto nos discos ensaiados com pinos de cobre quanto nos pinos ensaiados com pinos de alumínio observou-se a formação de filmes ricos em oxigênio. A formação de ilhas de cobre metálico provocou a instabilidade do comportamento do coeficiente de atrito do par cobre-aço, enquanto que o par alumínio-aço teve um comportamento mais estável devido as ilhas de óxido de alumínio. Nos ensaios utilizando pinos de latão, por sua vez, a presença de chumbo e oxidação moderada da superfície foi responsável pelo menor e mais estável coeficiente de atrito dos três pares tribológicos. O aumento da carga normal não alterou o comportamento do coeficiente de atrito, porém teve influência na formação das camadas de material aderido do pino na superfície dos discos.
Titre en anglais
Microstructural characterization of AISI 4140 steel metallic discs after pin on disc tribological tests using 6082-T6 aluminium, C10200 copper.
Mots-clés en anglais
Electron microscopy
Sliding friction
Sliding wear
Tribology
Resumé en anglais
Pin on disc tribotests were performed with copper, brass and aluminium pins tested against steel discs under normal loads between 10 and 50 N and characterized by means of laser interferometry and SEM. Copper-steel tribotests showed an unstable coefficient of friction curve around 0.65. Aluminium-steel and brass-steel tribopairs featured stable coefficient of friction curves, around 0.42 and 0.30, respectively. Both copper-steel and aluminiumsteel pairs presented oxygen rich transfer films. An adhesion of metallic copper patches caused the unstable coefficient of friction for the copper-steel, whereas for the aluminium-steel tribopair, the oxide layer controlled the coefficient of friction behaviour. An oxygen rich layer with some lead controlled the coefficient of friction for the brass-steel tribopair. Increasing the normal load did not affect the coefficient of friction but affect the formation of transfer layers.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2019-08-26
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.