Disertación de Maestría
DOI
https://doi.org/10.11606/D.3.2019.tde-26082019-100259
Documento
Autor
Nombre completo
Raphael Oliveira Ferreira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2019
Director
Tribunal
Azevedo, Cesar Roberto de Farias (Presidente)
Machado, Izabel Fernanda
Magnabosco, Rodrigo
Título en portugués
Caracterização microestrutural de discos metálicos de aço AISI 4140 após ensaios tribológicos do tipo pino-disco, usando pinos de alumí­nio 6082-T6, cobre C10200 e latão C36000.
Palabras clave en portugués
Materiais
Microscopia eletrônica
Tribologia
Resumen en portugués
Foram realizados ensaios tribológicos do tipo pino-disco com pinos de cobre puro, alumínio e latão para sob cargas normais de 10, 20 e 50 N contra discos de aço, que foram analisados após os ensaios utilizando interferometria óptica 3D e microscopia eletrônica de varredura. O par tribológico cobre-aço apresentou curva de coeficiente de atrito instável, com valor médio de 0,65. Os pares alumínio-aço e latão-aço apresentaram curvas de coeficiente de atrito mais estáveis que aquelas apresentadas nos ensaios com pinos de cobre, com valor médio de coeficiente de atrito de 0,42 e 0,30, respectivamente. Tanto nos discos ensaiados com pinos de cobre quanto nos pinos ensaiados com pinos de alumínio observou-se a formação de filmes ricos em oxigênio. A formação de ilhas de cobre metálico provocou a instabilidade do comportamento do coeficiente de atrito do par cobre-aço, enquanto que o par alumínio-aço teve um comportamento mais estável devido as ilhas de óxido de alumínio. Nos ensaios utilizando pinos de latão, por sua vez, a presença de chumbo e oxidação moderada da superfície foi responsável pelo menor e mais estável coeficiente de atrito dos três pares tribológicos. O aumento da carga normal não alterou o comportamento do coeficiente de atrito, porém teve influência na formação das camadas de material aderido do pino na superfície dos discos.
Título en inglés
Microstructural characterization of AISI 4140 steel metallic discs after pin on disc tribological tests using 6082-T6 aluminium, C10200 copper.
Palabras clave en inglés
Electron microscopy
Sliding friction
Sliding wear
Tribology
Resumen en inglés
Pin on disc tribotests were performed with copper, brass and aluminium pins tested against steel discs under normal loads between 10 and 50 N and characterized by means of laser interferometry and SEM. Copper-steel tribotests showed an unstable coefficient of friction curve around 0.65. Aluminium-steel and brass-steel tribopairs featured stable coefficient of friction curves, around 0.42 and 0.30, respectively. Both copper-steel and aluminiumsteel pairs presented oxygen rich transfer films. An adhesion of metallic copper patches caused the unstable coefficient of friction for the copper-steel, whereas for the aluminium-steel tribopair, the oxide layer controlled the coefficient of friction behaviour. An oxygen rich layer with some lead controlled the coefficient of friction for the brass-steel tribopair. Increasing the normal load did not affect the coefficient of friction but affect the formation of transfer layers.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-08-26
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.