Thèse de Doctorat
DOI
10.11606/T.3.2012.tde-26072013-142354
Document
Auteur
Nom complet
Eduardo Franco de Monlevade
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2012
Directeur
Jury
Goldenstein, Hélio (Président)
Abreu, Hamilton Ferreira Gomes de
Hupalo, Marcio Ferreira
Landgraf, Fernando José Gomes
Tschiptschin, André Paulo
Titre en portugais
Estudo das transições morfológicas na decomposição da austenita utilizando um par de difusão Fe-5%Ni/Fe-10%Ni.
Mots-clés en portugais
Aço
Aço níquel
Transformação de fase
Tratamento térmico
Resumé en portugais
No presente trabalho, foram estudados os aspectos morfológicos da decomposição da austenita em função da variação dos teores de níquel e carbono. Para a realização deste estudo, foi preparado um par de difusão composto de ligas Fe-5%Ni e Fe-10%Ni. O par foi feito por co-laminação a quente, e amostras deste par foram carburadas até teores de carbono de 0,1%, 0,3%, 0,5%C e 0,7%C. As amostras foram austenitizadas a 900°C por 20 minutos e tratadas isotermicamente por 10 minutos a temperaturas entre 400°C e 500°C por 10 minutos. Nas ligas hipoeutetóides, os produtos de decomposição da austenita predominantes são perlita degenerada, bainita inferior e ferrita degenerada. A perlita degenerada foi observada nas amostras tratadas a 500°C, nas regiões de baixo níquel, juntamente com a bainita superior. À medida em que se avança para regiões de mais alto níquel, a formação de perlita degenerada cessa, sendo a bainita o único produto de decomposição. A bainita dá então lugar à formação de ferrita degenerada, isenta de carbonetos, em regiões de teor de níquel próximo de 7%. Nas amostras tratadas a 400°C, o principal produto de decomposição da austenita é a bainita inferior, cuja escala se torna progressivamente mais grosseira com o aumento do teor de níquel. Foi observado um produto de decomposição eutetóide que pode ser caracterizado como bainita nodular, mas que só ocorre em estágios avançados dar reação de decomposição da austenita. Análises de difração de elétrons retroespalhados revelam que a ferrita degenerada é composta de múltiplas partículas de ferrita, que têm entre si uma diferença de orientação cristalográfica de até 8°. Nas ligas hipereutetóides, os produtos de decomposição da austenita são perlita e bainita inversa. Com a diminuição da temperatura de tratamento, nota-se uma diminuição na formação de perlita, sendo esta totalmente suprimida a 400°C. Em todas as amostras tratadas, a decomposição da austenita não foi completa após 10 minutos de tratamento térmico, independente da temperatura de tratamento.
Titre en anglais
Study of the morphological transitions in austenite decomposition using a Fe-5%Ni/Fe-10%Ni diffusion couple.
Mots-clés en anglais
Heat treatment
Nickel steel
Phase transformations
Steel
Resumé en anglais
In the present work, the morphological aspects of austenite decomposition were studied as related to Ni and C. To perform this study, a diffusion couple composed of Fe-5%Ni and Fe-10%Ni was produced. The couples were produced by hot co-rolling, and carburized to carbon contents of 0.1%C, 0.3%C, 0.5%C and 0.8%C. The samples were solution treated in the austenitic range at 900°C for 20 minutes, and held isothermally at temperatures between 400°C and 500°C for 10 minutes. In the hypoeutectoid alloys, the austenite decomposition products are degenerate pearlite, bainite (upper and lower), and degenerate ferrite. Degenerate pearlite was observed in the samples treated at 500°C and 450°C, and only in the low-nickel regions, along with upper bainite. With increasing nickel content, the formation of degenerate pearlite ceases, and bainite is the only decomposition product. Bainite is then replaced by degenerate ferrite, free of carbides, at nickel contents close to 7%. In the samples treated at 400°C, the main decomposition product is lower bainite, with a progressively coarser scale as the nickel content rises. A nodular decomposition product was observed, which can be identified as nodular bainite, occurring only at advanced stages of reaction in samples treated at 400°C. Electron backscatter diffraction analyses reveal that degenerate ferrite is characteristically composed of multiple ferrite particles, containing a crystallographic misorientation of up to 8°. In hypereutectoid alloys, the decomposition products are pearlite and inverse bainite. As the treatment temperature is diminished, a decrease in the amount of pearlite formed is observed, and pearlite is completely suppressed at 400°C. In all samples treated, the reaction was incomplete after 10 minutes, regardless of the temperature of isothermal hold.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2013-08-05
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2023. Tous droits réservés.