Tesis Doctoral
DOI
10.11606/T.3.2012.tde-26072013-142354
Documento
Autor
Nombre completo
Eduardo Franco de Monlevade
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2012
Director
Tribunal
Goldenstein, Hélio (Presidente)
Abreu, Hamilton Ferreira Gomes de
Hupalo, Marcio Ferreira
Landgraf, Fernando José Gomes
Tschiptschin, André Paulo
Título en portugués
Estudo das transições morfológicas na decomposição da austenita utilizando um par de difusão Fe-5%Ni/Fe-10%Ni.
Palabras clave en portugués
Aço
Aço níquel
Transformação de fase
Tratamento térmico
Resumen en portugués
No presente trabalho, foram estudados os aspectos morfológicos da decomposição da austenita em função da variação dos teores de níquel e carbono. Para a realização deste estudo, foi preparado um par de difusão composto de ligas Fe-5%Ni e Fe-10%Ni. O par foi feito por co-laminação a quente, e amostras deste par foram carburadas até teores de carbono de 0,1%, 0,3%, 0,5%C e 0,7%C. As amostras foram austenitizadas a 900°C por 20 minutos e tratadas isotermicamente por 10 minutos a temperaturas entre 400°C e 500°C por 10 minutos. Nas ligas hipoeutetóides, os produtos de decomposição da austenita predominantes são perlita degenerada, bainita inferior e ferrita degenerada. A perlita degenerada foi observada nas amostras tratadas a 500°C, nas regiões de baixo níquel, juntamente com a bainita superior. À medida em que se avança para regiões de mais alto níquel, a formação de perlita degenerada cessa, sendo a bainita o único produto de decomposição. A bainita dá então lugar à formação de ferrita degenerada, isenta de carbonetos, em regiões de teor de níquel próximo de 7%. Nas amostras tratadas a 400°C, o principal produto de decomposição da austenita é a bainita inferior, cuja escala se torna progressivamente mais grosseira com o aumento do teor de níquel. Foi observado um produto de decomposição eutetóide que pode ser caracterizado como bainita nodular, mas que só ocorre em estágios avançados dar reação de decomposição da austenita. Análises de difração de elétrons retroespalhados revelam que a ferrita degenerada é composta de múltiplas partículas de ferrita, que têm entre si uma diferença de orientação cristalográfica de até 8°. Nas ligas hipereutetóides, os produtos de decomposição da austenita são perlita e bainita inversa. Com a diminuição da temperatura de tratamento, nota-se uma diminuição na formação de perlita, sendo esta totalmente suprimida a 400°C. Em todas as amostras tratadas, a decomposição da austenita não foi completa após 10 minutos de tratamento térmico, independente da temperatura de tratamento.
Título en inglés
Study of the morphological transitions in austenite decomposition using a Fe-5%Ni/Fe-10%Ni diffusion couple.
Palabras clave en inglés
Heat treatment
Nickel steel
Phase transformations
Steel
Resumen en inglés
In the present work, the morphological aspects of austenite decomposition were studied as related to Ni and C. To perform this study, a diffusion couple composed of Fe-5%Ni and Fe-10%Ni was produced. The couples were produced by hot co-rolling, and carburized to carbon contents of 0.1%C, 0.3%C, 0.5%C and 0.8%C. The samples were solution treated in the austenitic range at 900°C for 20 minutes, and held isothermally at temperatures between 400°C and 500°C for 10 minutes. In the hypoeutectoid alloys, the austenite decomposition products are degenerate pearlite, bainite (upper and lower), and degenerate ferrite. Degenerate pearlite was observed in the samples treated at 500°C and 450°C, and only in the low-nickel regions, along with upper bainite. With increasing nickel content, the formation of degenerate pearlite ceases, and bainite is the only decomposition product. Bainite is then replaced by degenerate ferrite, free of carbides, at nickel contents close to 7%. In the samples treated at 400°C, the main decomposition product is lower bainite, with a progressively coarser scale as the nickel content rises. A nodular decomposition product was observed, which can be identified as nodular bainite, occurring only at advanced stages of reaction in samples treated at 400°C. Electron backscatter diffraction analyses reveal that degenerate ferrite is characteristically composed of multiple ferrite particles, containing a crystallographic misorientation of up to 8°. In hypereutectoid alloys, the decomposition products are pearlite and inverse bainite. As the treatment temperature is diminished, a decrease in the amount of pearlite formed is observed, and pearlite is completely suppressed at 400°C. In all samples treated, the reaction was incomplete after 10 minutes, regardless of the temperature of isothermal hold.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-08-05
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.