Disertación de Maestría
DOI
10.11606/D.3.2013.tde-26062014-220239
Documento
Autor
Nombre completo
Priscila Alves Martins
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Tenório, Jorge Alberto Soares (Presidente)
Bartoli, Julio Roberto
Valera, Ticiane Sanches
Título en portugués
Uso de aditivos não tóxicos como retardantes de chama em ABS.
Palabras clave en portugués
ABS
Aditivos retardantes de chama não halogenados
Compósitos
Nanocompósitos
Resumen en portugués
Os retardantes de chama são usados em diversos produtos, especialmente na indústria de eletroeletrônico. A irrevogável finalidade dos retardantes é proteger a vida das pessoas, reduzindo ferimentos e a destruição de propriedades. Contudo, devido à percepção dos riscos ambientais e toxicológicos presentes nas composições comerciais halogenadas e tóxicas, o seu uso está sendo proibido. Apesar da comum comercialização, novas pesquisas têm se desenvolvido visando à substituição destes retardantes, acompanhando medidas legais. Este trabalho visa estudar uma alternativa de aditivo retardante de chama livre de halogênio, tendo como matriz polimérica o copolímero de ABS, combinando aditivos: argila organofílica Cloisite 20A, argila Cloisite Na+ tratada com sal quaternário de fosfônio, polifosfato de amônio, melamina, partículas micrométricas e nanométricas de hidróxido de alumínio, dióxido de titânio e sílica formando assim um compósito. Para a caracterização foram realizados ensaios de térmicos de TGA e DSC, ensaios mecânicos de resistência à tração e resistência ao impacto Izod sem entalhe, avaliação da morfologia através de MEV e MEV-FEG, análise de difração de Raios-X (DRX), espectroscopia de infravermelho acoplado ao acessório de reflexão atenuada (FTIR-ATR), ensaios de retardância à chama com base na norma ASTM D635-10 e norma UL 94. Por meio dos resultados foi possível observar efeitos da adição dos aditivos na obtenção de compósitos de ABS com aditivos retardante de chama inertes, que atingiram classificação V-0 e V-2 na Ul 94, com redução da velocidade propagação da chama entre 18% e 80% conforme a ASTM D635.
Título en inglés
Use of additives no toxic with flame retardant at ABS.
Palabras clave en inglés
ABS
Composite
Halogen free flame retardance additives
Nanocomposites
Resumen en inglés
The flame retardant are used in several products, specialty for electrical and electronics industry. The irrevocable finality from flame retardant is fires protection to help safeguard of people, reduce injury and reduce destruction of property. However, due the perception of environmental risk and toxicity in composites commercial with halogen and toxic, it has been prohibited. Despite the common commercialization news researches has been developing to substitute this flame retardant, together accompany the new position of law. This work wanted to study an alternative of additive free halogen flame retardant, with polymer matrix the ABS copolymer, combinations the additive: organoclay Cloisite 20A, organoclay Cloisite Na+ treated with quaternary phosphonium salt, ammonium polyphosphate, melamine, micrometric and nanometric particles of aluminum hydroxide, titanium dioxide and silica forming that a composite. To characterization was doing thermal test of TGA and DSC, mechanical test of tensile and impact Izod strength, morphologia available through of MEV and MEV-FEG, X-ray diffraction analysis(XRD), infrared spectroscopy with attenuated total reflectance accessory (FTIR-ATR), flame retardant test based the ASTM D635-10 norm and UL 94 norm. Although the result was possible to observe effects about the addition the additive to obtain the ABS composite with inert flame retardant additives, that achieved V-0 and V-2 on the Ul 94, with reduction of linear burning rate between 18% to 80% from ASTM D635.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-07-02
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.