Master's Dissertation
DOI
10.11606/D.3.2017.tde-25072017-093151
Document
Author
Full name
Angelo Fernando Padilha
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 1977
Supervisor
Committee
Falleiros, Ivan Gilberto Sandoval (President)
Finardi, Jorge
Lorente, Gustau Ferran
Title in Portuguese
Competição entre recuperação e recristalização em uma liga de alumínio contendo dispersão de precipitados.
Keywords in Portuguese
Alumínio
Ligas metálicas
Recristalização
Abstract in Portuguese
Através de microscopia ótica utilizando luz polarizada e de metalografia quantitativa, determinou-se a cinética de recristalização a 400 ºC de uma liga de alumínio da série 3000 contendo dispersão de precipitados, para diferentes graus de deformação produzidos por laminação. Mediram-se parâmetros, para vários tempos de recozimento, que permitiram determinar: fração volumétrica recristalizada, quantidade de interfaces por unidade de volume entre regiões recristalizadas e não recristalizadas e, entre regiões recristalizadas, assim como velocidade média de migração de interfaces. Fizeram-se também medidas de microdureza em todas as amostras. Os resultados experimentais mostraram que à medida que se diminui o grau de deformação, a quantidade de interfaces por unidade de volume responsáveis pela recristalização diminui exigindo portanto um crescimento através de distâncias maiores para a recristalização se completar, tornando a cinética de recristalização mais dependente do crescimento. Constatou-se a ocorrência de recuperação, durante a recristalização, das regiões não recristalizadas e consequente diminuição da velocidade média de migração de interfaces com o tempo de recozimento. Com a diminuição da deformação, ocorreram frações não recristalizadas residuais, as quais eram maiores para graus de deformação menores, chegando a atingir mais de 80% para 34,4% de redução em espessura. Os resultados sugerem que, para baixas deformações, a velocidade de crescimento tem um papel importante na cinética de recristalização de ligas com dispersão de precipitados. A comparação entre os resultados de metalografia quantitativa e medidas de microdureza evidenciou algumas limitações desta última técnica para estudo de recristalização.
Title in English
Competition between recovery and recrystallization in a dispersion hardened aluminium alloy.
Keywords in English
Aluminium alloy AA 3003
Recovery
Recrystallization
Abstract in English
Using polarized light optical micrsocopy and quantitative metalography, kinetics of recrystallization at 400 ºC of an aluminum alloy of 300 series were determined, for different rolling deformation. Recrystallized volume fraction, amount of interfaces per unit volume, between recrystrallized and unrecrystallized regions and between recrystallized grains, and also mean velocity of interface migration were determined. Microhardness measurements were made in all specimens. The results have shown that with decreading deformation, the amount of interfaces responsible for recrystallization, per unit volume, decreases and so the interfaces must sweep larger distances for complete recrystallization, making kinetics more dependent on growth. Recovery of the unrecrystallized regions was observed, during recrystallization, causing decrease in the average velocity of interface migration with annealing time. With decreasing deformation residual unrecrystallized volumes have been observed, after long time anneals. The fraction of residual unrecrystallized region were large than 80-% for 34,4% thickness reduction. The results suggest that, in alloys with precipitates, the growth velocity has an important role in recrystallization kinetics. Some shortcomings of hardness measurements, as a tool to study recrystallization, were shown by comparison between the quantitative metallography and hardness measurements.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2017-07-25
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.