• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
https://doi.org/10.11606/D.3.2019.tde-23102019-145659
Documento
Autor
Nombre completo
Lucas Narcizo de Moura
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2019
Director
Tribunal
Valera, Ticiane Sanches (Presidente)
Silva, Leonardo Gondim de Andrade e
Souza, Adriana Martinelli Catelli de
 
Título en portugués
Estudo de um método simples para produção de nanocompósitos de grafeno multicamadas no poliestireno-bloco-polibutadieno-bloco-poliestireno.
Palabras clave en portugués
Elastômeros
Grafeno Multicamadas (GMC)
Nanocompósitos
Poliestireno-bloco-polibutadieno-bloco-poliestireno (SBS)
Resumen en portugués
Nessa dissertação, o grafeno multicamadas (GMC) foi obtido por meio de sonicação direta em N-metil-2-pirrolidona (NMP), utilizando ultrassom de ponteira, na presença de poliestireno-bloco-polibutadieno-bloco-poliestireno (SBS). O nanocompósito de SBS com 12,4% em massa de GMC foi produzido por co-coagulação e posteriormente processado termicamente em extrusora dupla rosca com mais SBS, formando nanocompósitos com 0,5% e 1,0% em massa de GMC. As micrografias obtidas por microscopia eletrônica de transmissão (MET) e microscopia eletrônica de varredura (MEV) indicaram a presença de grafeno e GMC dispersos na matriz polimérica. Os resultados obtidos por espectroscopia vibracional de absorção no infravermelho com transformada de Fourier (FTIR) indicaram uma possível interação entre o grafeno e os blocos de poliestireno, o que pode ter auxiliado no processo de esfoliação. A análise termogravimétrica (TG) demonstrou que o processo tem rendimento compatível com outros processos de obtenção do grafeno. Os ensaios de tração e de dureza mostraram que o GMC pode ter efeito reforçante no nanocompósito. O processo com poucas etapas e com uso de poucos reagentes, desenvolvido nesse trabalho, mostrou-se uma alternativa promissora para produção de nanocompósitos de grafeno em grande escala.
 
Título en inglés
Study of a simple method to produce multilayer graphene nanocomposites with polystyrene-block-polybutadiene-block-polystyrene.
Palabras clave en inglés
Multilayer Graphene (MLG)
Nanocomposites
Polystyrene-block-polybutadiene-block-polystyrene (SBS)
Thermoplastic elastomers
Resumen en inglés
In this work multilayer graphene (MLG) was obtained through direct sonication of graphite in N-methyl-2-pirrolidone (NMP) using probe sonicator in the presence of polystyrene-block-polybutadiene-block-polystyrene (SBS). The nanocomposite of SBS with 12.4 wt% GMC was produced by co-coagulation and further thermally processed in a twin-screw extruder with more SBS to obtain nanocomposites with 0.5 wt% and 1.0 wt% GMC. Transmission Electronic Microscopy (TEM) and Scanning Electronic Microscopy (SEM) has shown individuals graphene layers and MLG well dispersed in the polymer matrix. The Infrared Spectra (FTIR) suggested a good interaction between graphene and the polystyrene (PS) blocks, which may have improved the exfoliation process. The thermogravimetric analysis (TGA) demonstrated a good efficiency in the process. Tensile and hardness tests indicate the reinforcement effect of MLG in the nanocomposite. The few steps process developed in this work using few reagents had been shown as a promising large-scale process to produce graphene nanocomposites.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-10-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores.
CeTI-SC/STI
© 2001-2024. Biblioteca Digital de Tesis y Disertaciones de la USP.