Mémoire de Maîtrise
DOI
10.11606/D.3.2016.tde-21072016-092834
Document
Auteur
Nom complet
Satoru Yoshida
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2015
Directeur
Jury
Hui, Wang Shu (Président)
Onmori, Roberto Koji
Silva, Mauro Francisco Pinheiro da
Titre en portugais
Sistemas poliméricos à base de PEDOT:PSS para aplicação como circuitos e eletrodos de dispositivos.
Mots-clés en portugais
DMSO
Filmes finos
PEDOT:PSS
Polímeros (Materiais)
Resistência elétrica
Semicondutores
TRP2
Resumé en portugais
Este trabalho tem como objetivo estudar filmes finos de polímeros semicondutores preparados a partir de dispersões coloidais de poli(3,4 etilenodioxitiofeno)/poli(estirenosulfonato de sódio) (PEDOT:PSS), submetidos a tratamentos físico-químicos para alterar as suas características morfológicas e estruturais, melhorando a condutividade elétrica e mantendo um bom nível de transmitância óptica na faixa de comprimento de onda da luz visível. Foram utilizadas no estudo duas dispersões coloidais comerciais de PEDOT:PSS, identificadas como P1 e P2. O P1 descrito pelo fornecedor como de grau condutivo (1 S.cm-1) e P2 de grau altamente condutivo (<100 ?/?). Foram produzidos filmes finos em três procedimentos diferentes e realizadas medidas de resistência elétrica e transmitância óptica. Na primeira série, os filmes foram preparados por spin-coating da dispersão coloidal original de PEDOT:PSS e seguidos pelo recozimento na estufa. Na segunda série, foi adicionado à dispersão coloidal original de PEDOT:PSS um solvente orgânico polar, o dimetilsulfóxido (DMSO), após a centrifugação, a dispersão sobrenadante foi depositada para a preparação de filmes finos como descrito na etapa anterior. Na terceira série, à parte sobrenadante da dispersão coloidal de PEDOT:PSS preparada na segunda série, foi adicionada uma solução precursora de nanopartículas de prata (Tinta Reativa de Prata) (TRP2) e a dispersão coloidal foi depositada para formar filmes finos como descrito anteriormente. As resistividades elétricas com os valores mais significativos foram de filmes de P1 e de P2 depositados a 2000 rpm. Para P1 foram observadas resistividades de 1,37 ?.cm, 0,34 ?.cm e 0,18 ?.cm, para as dispersões coloidais P1 original, P1 tratado com DMSO e P1 tratado com DMSO/TRP2, respectivamente, correspondendo a uma redução de 87% do valor da resistência elétrica da primeira para a terceira série. A transmitância óptica dos filmes a 550 nm se manteve entre 80~90% para todas as séries, nas análises por espectroscopia no UV-Vis. Para os filmes de P2, depositadas a 2000 rpm, as resistividades elétricas nos filmes foram de 0,76 ?.cm, 0,015 ?.cm e 0,0012 ?.cm, para P2 original, P2 tratado com DMSO e P2 tratado com DMSO/TRP2, respectivamente, correspondendo a uma redução de 99,8% do valor da resistência elétrica da primeira para a terceira série. O valor da transmitância óptica dos filmes a 550 nm manteve-se entre 85~90% na primeira e segunda série, entretanto para os filmes da terceira série, devido à presença da fase prata grosseira, reduziu-se para o intervalo entre 40~60%.
Titre en anglais
Polymer systems based on PEDOT;PSS for use in circuits and electrode devices.
Mots-clés en anglais
DMSO
Electrical resistance
PEDOT:PSS
TRP2
Resumé en anglais
This work aims to study thin films of semiconducting polymers prepared from colloidal dispersions of poly(3,4-ethylenedioxythiophene)/poly(styrenesulfonate) (PEDOT: PSS), submitted to physicochemical treatments in order to change their microstructural features and improve their electrical conductivity, while maintaining a good level of optical transmittance in the visible wavelength range. Two types of commercial colloidal dispersions of PEDOT:PSS were used in the study, named as P1 and P2. The P1 is described as a conductive grade (250 ?/?) and P2, highly conductive grade (<100 ?/?). Thin films were produced from colloidal dispersions through three different procedures and their electrical resistance and optical transmittance were measured. In the first series, films were prepared by spin-coating of the PEDOT: PSS pristine colloidal dispersion, followed by annealing in the oven. In the second series, to the pristine colloidal dispersion of PEDOT:PSS a polar organic solvent dimethylsulfoxide (DMSO) was added, then after centrifugation, the supernatant colloidal dispersion was deposited to form thin films as described previously. In the third series, to the supernatant colloidal dispersion of PEDOT:PSS prepared in the second series, a silver nanoparticle precursor solution (Reactive Silver Ink) (TRP2) was added and the colloidal dispersion was deposited to form thin films as described previously. Electrical resistivity with the most significant values from P1 and P2 films deposited at 2000 rpm. For the films from P1, 1.37 ?.cm, 0.34 ?.cm and 0.18 ?.cm were observed, for pristine colloidal dispersion, with DMSO and with DMSO and TRP2, respectively; corresponding to a reduction of 87% of the electrical resistance from the first to the third series. The optical transmittance of films at 550 nm, as measured by UV-Vis spectroscopy, was maintained in the range 80~90% for all series. For the films from P2, the electrical resistances were observed to vary from 0.76 ?.cm to 0.015 ?.cm and 0.0012 ?.cm, for pristine P2 colloidal dispersion, after DMSO addition and with DMSO and TRP2, respectively, corresponding to a reduction of 99.8% in the electrical resistance from the first series to the third one. The optical transmittance of films at 550 nm was observed to remain in the range 85~90% for the first and second series, while the third series, due to the massive presence of a coarse silver phase, dropped to the range 40~60%.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
SatoruYoshida2015.pdf (3.57 Mbytes)
Date de Publication
2016-07-21
 
AVERTISSEMENT: Le matériau se réfère à des documents provenant de cette thèse ou mémoire. Le contenu de ces documents est la responsabilité de l'auteur de la thèse ou mémoire.
  • Santos, E R, et al. Comparação de diferentes eletrodos anodos utilizados em dispositivos OLEDs flexíveis. Revista Lumière , 2013, vol. 15, p. 54-72.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.