Master's Dissertation
DOI
10.11606/D.3.2012.tde-19112012-125104
Document
Author
Full name
Tiago Evangelista Gomes
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2012
Supervisor
Committee
Padilha, Angelo Fernando (President)
Plaut, Ronald Lesley
Rossi, Jesualdo Luiz
Title in Portuguese
Efeitos da temperatura de laminação na formação e na reversão de martensita induzida por deformação no aço inoxidável austenítico AISI 304L.
Keywords in Portuguese
Aço inoxidável austenítico 304L
Endurecimento por deformação
Martensita induzida por deformação
Recristalização
Refino de grão
Reversão da martensítica
Abstract in Portuguese
Objetivo principal desta dissertação foi verificar os efeitos da temperatura de laminação na formação de martensita induzida por deformação e na sua posterior reversão da martensita para austenita no aço inoxidável austenítico AISI 304L. O estudo foi predominantemente microestrutural e para análise e caracterização foram utilizadas as técnicas de microscopia óptica, microscopia eletrônica de varredura, difração de raios X, medidas de dureza Vickers e medidas de fases ferromagnéticas por ferritoscopia. As amostras foram inicialmente solubilizadas a 1100 ºC por uma hora, visando a dissolução de uma pequena quantidade residual de ferrita encontrada nas amostras na condição como recebida, depois laminadas em diferentes temperaturas, determinando-se curvas de endurecimento por deformação e de formação de martensita induzida por deformação em função do grau de deformação. Em seguida, foram realizados pré-recozimentos a 600 ºC, favorecendo apenas a reversão da martensita para austenita, de maneira que não ocorresse a recristalização. A quantidade e a temperatura de deformação apresentaram forte influência na quantidade de martensita formada, no endurecimento por deformação e na cinética de amolecimento durante o recozimento. Os pré-tratamentos realizados a 600 ºC causaram acentuada reversão da martensita, algum amolecimento e pequeno efeito no tamanho de grão recristalizado durante o posterior recozimento a 600 ºC.
Title in English
Effects of the rolling temperature on the formation and on the reversion of strain induced martensite in a AISI 304L stainless steel.
Keywords in English
304L austenitic stainless steel
Grain refinement
Martensite reversion
Recrystallization
Strain hardening
Strain induced martensite
Abstract in English
The main objective of the present dissertation was to verify the effects of the rolling temperature on the formation of strain induced martensite and in its subsequent martensite reversion to austenite in a AISI 304L stainless steel. The study was predominantly microstructural and, for the analysis and characterization, several techniques have been used, namely optical microscopy, scanning electron microscopy, X-ray diffraction, Vickers hardness measurements and magnetic phase measurements, using the ferritoscope. The samples were initially solution annealed at 1100 ºC for one hour, aiming at the dissolution of a small quantity of the residual -ferrite found in the samples in the as-received condition; then rolling was performed at different temperatures, evaluating strain hardening and the strain induced martensite as a function of strain. Following, pre-annealing treatments at 600 ºC have been performed, favoring only the martensite to austenite reversion, in a way that no recrystallization would occur. Strain and temperature had a strong influence on the amount of formed martensite, on the strain hardening and on the softening kinetics during annealing. The pre-annealing treatments at 600 ºC caused an accentuated effect on the martensite reversion, some softening and a small effect on the recrystallized grain size during the subsequent annealing at 600 ºC.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2012-11-27
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2022. All rights reserved.