Disertación de Maestría
DOI
https://doi.org/10.11606/D.3.1999.tde-18112020-095449
Documento
Autor
Nombre completo
André de Albuquerque Vicente
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1999
Director
Tribunal
Tenório, Jorge Alberto Soares (Presidente)
Falleiros, Neusa Alonso
Ramanathan, Lalgudi Venkataraman
Título en portugués
Oxidação ao ar a altas temperaturas de ligas à base de níquel.
Palabras clave en portugués
Alta temperatura
Níquel
Oxidação
Resumen en portugués
O presente trabalho enfoca a oxidação a alta temperatura de ligas do sistemas Ni-Al e Ni-Cr-Al. As ligas estudadas foram o Inconel 713C, o IC50 e uma liga experimental baseada no intermetálico Ni3Al com adição de Cr denominada liga X. Todas as ligas foram oxidadas ao ar durante 24 horas, nas temperaturas 800, 900, 1000, 1100, 1200 e 1300ºC, sempre em uma microbalança termogravimétrica (TG). Estes ensaios tiveram suas curvas de ganho de massa registradas em um microcomputador, que é conectado à TG através de uma interface. A superfície oxidada das ligas foi analisada por difração de raios-X e no microscópio eletrônico de varredura (MEV) foi examinada a seção transversal, permitindo a observação morfológica das camadas formadas. Durante este exame foram realizadas micro-análises EDS nas camadas de óxido formadas. Todos ensaios de oxidação ao ar apresentaram cinéticas de crescimento parabólicas desprezando-se as etapas iniciais de formação dos óxidos. Para a liga IC50 foram identificados os óxidos NiO e Al2O3. Para a liga Inconel 713C e liga X foram identificados os óxidos NiO, Al2O3 e Cr2O3. A liga IC50 apresentou comportamento bimodal parabólico. A liga Inconel 713C apresentou o melhor comportamento quanto à oxidação a alta temperatura, ou seja, a menor constante de crescimento parabólico (Kp) das três ligas em estudo para todas as temperaturas de ensaio. Este comportamento da liga Inconel 713C deve-se à formação de uma película contínua e não-porosa de Al2O3. Devido à formação inicial de uma película de NiO e posterior formação de Al2O3 e/ou Cr2O3 , foram observados comportamentos complexos para todas as cinéticas de oxidação das ligas estudadas.
Título en inglés
High temperatures oxidation in air of nickel based alloys
Palabras clave en inglés
Inconel 713
Kinetics
Ni3Al
Nickel-based alloys
Oxidation at high temperatures
Resumen en inglés
The present investigation focuses the high-temperature oxidation of alloys Ni-Al and Ni-Cr-Al. These alloys were Inconel 713C, IC50 and an experiment alloy based on Ni3Al with addition of Cr called alloy X. All alloys were oxidized in air for 24 hours at 800, 900, 1000, 1100, 1200 and 1300ºC, using a thermogravimetric analyser (TGA). The weight gain curves of these oxidation tests were registered in a microcomputer connected to the TGA through a specific interface. The oxidized surfaces of tested samples were analyzed by X-ray diffraction (XRD), while the morphology of scales were examined with the scanning electron microscope (SEM). During the SEM analysis the samples were also submited to energy dispersive spectrometry (EDS) microanalysis. All the the alloys tested in air showed parabolic kinetics when disregarded the initial stages of scales formation. IC50 showed formation of NiO and Al2O3 scales. Inconel 713C and alloy X showed formation of NiO, Al2O3 and Cr2O3 scales. IC50 showed a bimodal parabolic behaviour. Inconel 713C showed the best high-temperature oxidation resistance due the formation of a continuous and non-porous scale of Al2O3. Due the initial formation of NiO scales and subsequent formation of Al2O3 and/or Cr2O3 scales, all alloys showed complex behaviours.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2020-11-18
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • A.A.VICENTE,, ESPINOSA, D. C. R., e Tenório, Jorge Alberto Soares. Caracterização dos óxidos formados após ensaio de oxidação ao ar a 1300C da liga Iconel 713C, do intermetálico Ni3Al e de uma nova liga experimental baseada no intermetálico Ni3Al. In Congresso Anual da Associação Brasileira de Metalurgia e Materiais - 55, Rio de Janeiro, 2000. Congresso Anual da Associação Brasileira de Metalurgia e Materiais - 55., 2000.
  • A.A.VICENTE,, ESPINOSA, D. C. R., e Tenório, Jorge Alberto Soares. Estudo da Cinética de Oxidação ao Ar a Altas Temperatura da Liga IC-50. In Congresso Anual da Associação Brasileira de Metalurgia e Materiais - 55, Rio de Janeiro, 2000. Congresso Anual da Associação Brasileira de Metalurgia e Materiais - 55., 2000.
  • Tenório, Jorge Alberto Soares, A.A.VICENTE,, e ESPINOSA, D. C. R. Oxidação ao Ar e Altas Temperaturas da Superligas à Base de Níquel Inconel 713 C. In Congresso Anual da Associação Brasileira de Metalurgia e Materiais - 55, Rio de Janeiro, 2000. Congresso Anual da Associação Brasileira de Metalurgia e Materiais - 55., 2000.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.