• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.3.2009.tde-18112009-102050
Documento
Autor
Nombre completo
Luís Augusto Batista de Moraes
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Tenório, Jorge Alberto Soares (Presidente)
Capocchi, José Deodoro Trani
Vieira, Claudio Batista
Título en portugués
Caracterização de macro e micro-inclusões em aços acalmados ao alumínio produzidos por lingotamento contínuo.
Palabras clave en portugués
Aço (refino)
Resumen en portugués
Neste trabalho foram estudadas 10 corridas em duas usinas siderúrgicas semi-integradas, de aço baixa liga para uso em construção mecânica. Em cada uma das corridas foram retiradas 9 amostras, cada uma ao final de uma etapa do processo de produção: após a remoção de escória na panela, antes da desgaseificação a vácuo, após a desgaseificação a vácuo, após a adição de arame de Al, após a adição de arame de CaSi, após a adição de arame de S, após o fim da turbulência no distribuidor no lingotamento contínuo, 30 minutos após o fim da turbulência no distribuidor no lingotamento contínuo, e 60 minutos após o fim da turbulência no distribuidor no lingotamento contínuo. As amostras foram preparadas metalograficamente e analisadas ao microscópio eletrônico de varredura (MEV) com espectrometria de dispersão de energia (EDS), a fim de se identificar as inclusões presentes no aço em cada etapa do processo. Com isto pode-se fazer a caracterização das inclusões encontradas em cada etapa do processo e a sua classificação segundo a composição química e morfologia. Através da comparação da composição química das inclusões encontradas ao final do refino e no lingotamento contínuo foi possível verificar uma tendência de formação de inclusões de espinélio, e através da composição química das inclusões encontradas no lingotamento contínuo foi possível identificar em quais das corridas estudadas houve a presença de inclusões de aluminatos de cálcio formados no estado líquido.
Título en inglés
Characterization of macro and micro inclusions in Al-killed steels produced by continuous casting.
Palabras clave en inglés
Characterization
Non-metallic inclusions
Steel (refining)
Resumen en inglés
In the present work it was studied 10 heats in two steelworks, of low alloyed steel for use in mechanical construction. From each heat were taken 9 samples, each one of them at end of one production stage: after deslagging in the ladle; before vacuum degassing; after vacuum degassing; after Al wire addiction; after CaSi wire addiction; after S wire addiction; after the end of tundish turbulence at continuously casting; 30 minutes after the end of tundish turbulence at continuously casting; and 60 minutes after the end of tundish turbulence at continuously casting. Samples were metallographic prepared and analyzed by scanning electronic microscopic (SEM) with energy dispersive X-ray spectroscopy (EDX), in order to identify the inclusions present in steel in each process stage. This allowed the founded inclusions in each process stage to be characterized and classified according to chemical composition and morphology. By comparing founded inclusions chemical composition at end of refining and continuous casting was possible to observe a tendency of formation of spinel inclusions, and by founded inclusions chemical composition in continuous casting was possible to identify in which studied heats there were presence calcium aluminates inclusions formed in the liquid state.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Luis_Moraes.pdf (19.00 Mbytes)
Fecha de Publicación
2010-05-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.