Disertación de Maestría
DOI
10.11606/D.3.2015.tde-16112015-002331
Documento
Autor
Nombre completo
Anderson Clayton Nascimento Ribeiro
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2015
Director
Tribunal
Brandi, Sergio Duarte (Presidente)
Ramalho, José Pinto
Schön, Claudio Geraldo
Título en portugués
Avaliação da soldagem do aço naval AH36 microligado soldado pelo processo arco submerso com um e dois arames.
Palabras clave en portugués
Aços microligados
Soldagem a arco
Resumen en portugués
Diversas pesquisas em processos de soldagem para construção naval concentram-se em reduzir peso, aumentar a eficiência de energia, melhorar a resistência à corrosão e à tenacidade, bem como reduzir custos e tempo na construção dos navios. O aço naval microligado, AH36, apresenta boa correlação entre estrutura, propriedades mecânicas e soldabilidade. Estas características se devem principalmente a redução dos teores de carbono em função do uso de elementos microligantes como V, Nb e Ti, e do tipo de processo de obtenção das chapas pelo processo termomecânico seguido de resfriamento acelerado (em inglês: Thermomechanical control process -TMCP). Assim, o objetivo deste trabalho é avaliar a soldagem do aço naval AH 36 pelo processo de arco submerso com um e dois arames. Para tanto foram empregados os ensaios mecânicos de tração, de dobramento e de dureza. A tenacidade foi determinada pelo ensaio de Charpy com entalhe em V. Para caracterização metalográfica foram aplicadas as seguintes técnicas: Microscopia óptica (MO) e Microscopia eletrônica de varredura (MEV) e difração de raios X. Os resultados mostraram que as juntas soldadas apresentaram limite de resistência máxima de 561 MPa, com rompimento localizado no metal de base. No ensaio de microdureza foi observado que a região de crescimento de grão da zona afetada pelo calor, no experimento com a técnica Tandem, apresentou-se a região mais rígida das juntas analisadas, também o valor de microdureza no metal de solda foi 10% maior que no metal de base. Os resultados dos ensaios de impacto Charpy V mostraram que a temperatura de transição dúctil frágil do metal de base é de -30ºC. Da mesma maneira, o menor valor de energia absorvida foi para região do metal de solda. Através da análise da micrografia foi possível identificar diferentes morfologias de ferrita, a presença de perlita e pequenas regiões de martensita, bem como a presença de agregados MA.
Título en inglés
Evaluate the welding microalloyed steel AH36 by submerged arc process with one and two wires.
Palabras clave en inglés
Arc welding
Microalloyed steel
Resumen en inglés
Several researches in welding processes for shipbuilding has been focusing on reducing weight, increasing energy efficiency, improving corrosion resistance and toughness as well as reducing costs and time in the construction of ships. The microalloyed steel AH36 shipbuilding presents a good correlation among structure, mechanical properties and weldability. These features are mainly because reduction in carbon content due to the use of microalloying elements such as V, Nb and Ti, together with the process of steel plates by thermomechanical control process (TMCP), Therefore, the objective of this study is to evaluate the welding of shipbuilding steel AH 36 by submerged arc process with one and two wires. It was utilized tests such as: tensile, bending and hardness tests. The toughness was determined by Charpy V-Notch test. The metallographic characterization was carried out by the following techniques: optical microscopy (OM) and scanning electron microscopy (SEM) and X-Rays diffraction. The results showed that the tensile test for welded joints presented maximum resistance limit of 561 MPa, and the rupture was located in the base metal. Microhardness test showed that the region of coarse grain of heat affected zone, in the tandem submerged arc welding (SAW), presented the hardest region of the welded joint, also the microhardness value in the weld metal was 10% greater than the metal base. Charpy V notch test tests depicted a ductile brittle transition temperature at about -30 ºC. In the same way, the lowest absorbed energy was identified in the weld metal region. Through microstructure characterization it was possible to identify different morphologies of ferrite, pearlite and the small presence of martensite, as well as, the presence of aggregates MA.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Dissertacao_acnr.pdf (10.82 Mbytes)
Fecha de Publicación
2015-11-25
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.