• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Doctoral Thesis
DOI
10.11606/T.3.2013.tde-15102014-163235
Document
Author
Full name
Angelo José de Oliveira Zimmermann
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2013
Supervisor
Committee
Padilha, Angelo Fernando (President)
Chaves, Ricardo Risso
Hupalo, Marcio Ferreira
Lima, Nelson Batista de
Plaut, Ronald Lesley
Title in Portuguese
Encruamento, recristalização e textura cristalográfica de zircônio puro e da liga Zircaloy-4.
Keywords in Portuguese
Engenharia metalúrgica
Ensaios da estrutura dos materiais
Materiais nucleares
Abstract in Portuguese
Este trabalho consiste em uma pesquisa experimental comparativa entre o zircônio puro e a liga comercial de aplicação nuclear Zircaloy-4, com ênfase nas características de encruamento, recristalização e textura cristalográfica. Foram utilizadas várias técnicas complementares de análise microestrutural tais como microscopia óptica, microscopia eletrônica de varredura com análise química de microrregiões por dispersão de energia de raios X característicos, difração de raios X, calorimetria exploratória diferencial, medidas de dureza e de condutividade elétrica. Para as determinações de macrotextura foi utilizado um goniômetro dedicado de raios X. No estado como recebido, enquanto o zircônio puro apresentava grãos recristalizados com diâmetro médio de aproximadamente 50μm, a liga apresentava granulação alfa em plaquetas grosseiras com diâmetro médio do pré-grão beta de aproximadamente 1,1mm. Experiências de laminação e a determinação de curvas de limite de redução sem a presença de trincas em função da temperatura mostraram que enquanto o zircônio puro apresentou níveis altos de plasticidade na temperatura ambiente, a liga Zircaloy-4 apresentou baixa ductilidade e muitas trincas. As ductilidades dos dois materiais, especialmente da liga Zircaloy-4, aumentaram significativamente a partir de 300°C. A 500°C as ductilidades de ambos são idênticas. Utilizando-se deformações e recozimentos diferenciados foram obtidas tiras de mesma espessura, com grãos equiaxiais e diâmetros médios de grão de aproximadamente 9µm para os dois materiais. Os estudos de recristalização revelaram que, enquanto para o zircônio puro a recuperação contribui significativamente para o amolecimento, no caso da liga Zircaloy-4, o amolecimento ocorre quase que exclusivamente por recristalização. As temperaturas de recristalização do zircônio puro foram mais baixas que as da liga. Os átomos de soluto em solução sólida foram responsáveis pelos dois efeitos concorrentes; aumento da energia armazenada na deformação e aumento da resistência à recristalização. Além da caracterização microestrutural mencionada, foram realizadas determinações de textura cristalográfica para os dois materiais em diferentes condições. Com relação às texturas de laminação do zircônio puro, para uma mesma temperatura, em cerca de 50% de redução a textura de laminado a frio {1 1 2 2} < 1 0 1 0 > já estava plenamente formada e se alterou muito pouco a partir desta redução, até cerca de 90%. Com o aumento de temperatura de deformação para a mesma redução, a textura de laminado a frio se manteve estável até 300°C. A amostra de Zircaloy-4 preparada para possuir um tamanho de grão de 9 m tinha uma textura próxima de {0 0 0 2} < 1 0 1 0 >, demonstrando que os tratamentos térmicos e mecânicos utilizados para obtenção dessa amostra foram eficientes na redução da textura de laminado a frio {1 1 2 2} < 1 0 1 0 >. Recozimentos com duração de uma hora a 550 e 575°C, tanto em zircônio puro como na liga Zircaloy-4, foram suficientes para provocar recristalização estática. A 600°C, uma mudança na orientação cristalográfica foi verificada em Zircaloy-4, tendendo a {0 0 0 2} < 1 0 1 0 >, enquanto em zircônio puro os planos basais continuam estáveis. O uso de funções de distribuição de orientação cristalográfica (FDOC) auxiliaram na detecção de um segundo grupo orientado, que tende à orientação {1 0 1 1} < 1 1 2 0 >, além do grupo que reforça as fibras D0 e Rf . A mudança de textura ocorreu durante o crescimento de grão em ambos os materiais. De um modo geral, os resultados mostraram que o zircônio puro tende a ser mais suscetível à recristalização e ao crescimento de grão do que a liga Zircaloy-4. Entretanto, tanto zircônio como a liga são resistentes à modificação de textura, sendo que esta ocorreu principalmente com o crescimento de grão, em temperaturas após a completa recristalização primária.
Title in English
Work hardening, recrystallization and crystallographic texture of pure zirconium and Zircaloy-4 alloy.
Keywords in English
Metallurgical engineering
Nuclear materials
Testing the structure of materials
Abstract in English
This work shows a comparative experimental research between pure zirconium and the nuclear-grade zirconium alloy Zircaloy-4. This work emphasizes the characteristics of strain hardening, recrystallization, and crystallographic texture. Was used several complementary techniques for microstructural analysis such as optical microscopy, scanning electron microscopy with chemical analysis (EDS), X-ray diffraction, differential scanning calorimetry, indentation hardness and electrical conductivity. For measurements of macrotexture was used a dedicated X-ray goniometer. In the as received state, while pure zirconium showed grains recrystallized with an average diameter of about 50µm, the alloy had rough alpha plates with average diameter of beta pregrain of about 1,1mm. Rolling experiments and determination of reduction limit curves without cracks as a function of temperature showed that while zirconium pure showed high levels of plasticity at room temperature, the alloy zircaloy-4 showed low ductility and many cracks. The ductilities of the two materials, mainly zircaloy-4, significantly increased from 300°C. At 500°C, the ductilities were identical. Using different strains and annealing were obtained strips of equal thickness, with equiaxed grains and grain average diameters of about 9µm for both materials. Recrystallization studies revealed that recovery contributes significantly to softening of pure zirconium. In the case of the alloy zircaloy-4, the softening occurs almost exclusively by recrystallization. The temperature of recrystallization of the pure zirconium were lower than the alloy. The solute atoms in the solid solution were responsible for the two competing effects, the increase of the strain energy stored and the increasing of recrystallization resistance. Crystallographic texture measurements were made for both materials under different conditions. With respect to the rolling textures of pure zirconium, in about 50% reduction of the cold-rolled texture {1 1 2 2} < 1 0 1 0 > was already fully formed and changed very little from this reduction to about 90%. With the increase of temperature strain to the same reduction, texture cold rolled remained stable up to 300°C. The sample of zircaloy-4 prepared to have a grain size of 9m had a texture close to {0 0 0 2} < 1 0 1 0 >, demonstrating that the thermal and mechanical treatments used to obtain this sample were effective in reducing texture of cold-rolled {1 1 2 2} < 1 0 1 0 >. One hour annealings at 550 and 575°C, in pure zirconium and Zircaloy-4, were suffcient to cause static recrystallization. At 600 °C a change in crystallographic orientation was seen in zircaloy-4, tends to {0 0 0 2} < 1 0 1 0 >, while in pure zirconium the basal planes remains stable. The use of orientation distribution functions (ODF) aided in the detection of a second oriented group, which tends to orientation {1 0 1 1} < 1 1 2 0 >, besides the group that reinforced D0 and Rf fibers. The change in texture occurred during the grain growth in both materials. In general, the results showed that pure zirconium tends to be more susceptible to recrystallization and grain growth than Zircaloy-4. Nevertheless, Both zinconium and Zircaloy-4 are resistant to texture changes. The texture changes occurred mainly in grain growth, at temperatures after complete recrystallization.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2014-10-31
 
WARNING: The material described below relates to works resulting from this thesis or dissertation. The contents of these works are the author's responsibility.
  • TERADA, Maysa, et al. Corrosion behavior of Eurofer 97 and ODS-Eurofer alloys compared to traditional stainless steels [doi:10.1007/s10800-011-0320-1]. Journal of Applied Electrochemistry [online], 2011, vol. 41, p. 951-959.
  • Zimmermann, Angelo J. O., et al. Os novos aços inoxidáveis EUROFER utilizados em fusão nuclear [doi:10.1590/S0370-44672010000200012]. Religião & Sociedade [online], 2010, vol. 63, p. 287-292.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.