• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.3.2008.tde-15082008-150104
Documento
Autor
Nombre completo
Theógenes Silva de Oliveira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Ferreira Neto, João Batista
Martorano, Marcelo de Aquino (Presidente)
Ierardi, Maria Clara Filippini
Título en portugués
Refino de silício por solidificação direcional.
Palabras clave en portugués
Fenômenos de transporte
Refino
Silício
Transformações de fase
Resumen en portugués
A demanda do silício de grau solar (SiGS) utilizado na indústria fotovoltaica cresce atualmente em uma média de 35% ao ano e a projeção para a próxima década é de constante crescimento. Entretanto, a disponibilidade de matéria-prima para a produção do SiGS não tem crescido na mesma taxa, resultando em uma elevação de seu custo. Logo, a obtenção de rotas alternativas menos onerosas para a produção do SiGS torna-se crucial, principalmente sendo o Brasil o 3o maior produtor mundial de silício de grau metalúrgico. Tendo como objetivo a purificação do silício, o presente trabalho de pesquisa apresenta um estudo detalhado da solidificação direcional do silício, que é uma das etapas utilizadas em todas as rotas alternativas atualmente pesquisadas com o objetivo de purificação. Este estudo foi realizado em um forno do tipo Bridgman vertical, onde o silício líquido contido em um molde foi extraído da região quente do forno, resultando em uma solidificação direcional controlada e ascendente. Dois tipos de silício foram escolhidos como material de entrada para o processo de refino: o silício de grau metalúrgico e o silício de grau metalúrgico pré-refinado por lixiviação. Quatro velocidades de extração do molde entre 5 a 110 mm/s foram empregadas nos ensaios. A macrossegregação de impurezas nos lingotes obtidos foi medida através de análises químicas e a estrutura metalúrgica observada através de macro e micrografias. Os lingotes solidificados com menor velocidade de extração, onde se observa evidências de uma interface sólido-líquido plana, apresentam um grau de refino superior aos de maior velocidade, que mostram evidências de uma interface celular ou dendrítica. As análises químicas mostram que, após a solidificação direcional, os teores de Fe, Al, Cr e Ti medidos nas regiões da base e central dos lingotes atingem níveis especificados para o SiGS por alguns autores.
Título en inglés
Silicon refining by directional solidification.
Palabras clave en inglés
Phase transformation
Refining
Silicon
Transport phenomena
Resumen en inglés
The demand for solar grade silicon (SiGS) in the photovoltaic industry has grown 35% per year and a constant growth rate is predicted for the next decade. The availability of feedstock to produce SiGS, however, has not grown at the same rate, resulting in increasing SiGS cost. Consequently, the development of less expensive alternative processing routes is of paramount importance to the photovoltaic industry in general, and particularly to Brazil, which is the 3rd largest producer of metallurgical grade silicon. The objective of the present work is to study the directional solidification of silicon, which is a step adopted in virtually all alternative processing routes under development to refine silicon. The directional solidification of silicon was carried out in a vertical Bridgman furnace, where liquid silicon was poured into a quartz mold, which was extracted at constant velocity from the hot region of the furnace, resulting in ascending directional solidification. Two types of feedstock silicon were used, namely, a metallurgical grade silicon that was refined by leaching prior to directional solidification and metallurgical grade silicon as-received from the manufacturer. The quartz molds with liquid silicon were extracted at four different velocities in the range from 5 to 110 mm/s. In the solidified silicon ingots, the macrosegregation of elements were measured using accurate analytical techniques, whereas the metallurgical structures were observed in macro and micrographs. The ingots solidified at lower extraction velocities, at which evidences of a planar solidliquid interface were observed, showed greater refining effect than those solidified at larger velocities, which showed evidences of a cellular or dendritic solid-liquid interface. The contents of Fe, Al, Cr, and Ti measured at the base and center portions of the solidified ingots comply with the specifications of SiGS proposed by some authors.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
DISSERTACAO_FINAL.pdf (10.22 Mbytes)
Fecha de Publicación
2008-08-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.