Disertación de Maestría
DOI
10.11606/D.3.2013.tde-15052014-162113
Documento
Autor
Nombre completo
Cristian Camilo Hernandez Diaz
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Coelho, Antonio Carlos Vieira (Presidente)
Antunes, Maria Lúcia Pereira
Valenzuela Díaz, Francisco Rolando
Título en portugués
Estudo da possibilidade de uso de lodo de esgoto e lama vermelha como matérias-primas cerâmicas.
Palabras clave en portugués
Lama vermelha (Reciclagem)
Lodo de esgoto (Reciclagem)
Materiais cerâmicos
Resumen en portugués
A questão ambiental é um tema muito importante em nossos dias, é por isso que muitas empresas têm interesse em valorizar seus resíduos, seja para minimizar custos ou para vender um produto que pode ser usado como matéria-prima em outras indústrias. O estabelecimento de uma legislação mais rigorosa sobre o destino final dos resíduos sólidos tem sido acompanhado, de uma progressiva rejeição das disposições tradicionalmente aceitas. Por isso é necessário estudar novas alternativas para a disposição de resíduos industriais e pesquisar algumas aplicações para transformá-los em materiais com um valor agregado. Este trabalho tem como objetivo estudar a incorporação de dois resíduos em massas cerâmicas: lodo gerado no processo de tratamento de esgoto doméstico e lama vermelha (resíduo do processo Bayer de produção de alumina). Além desses resíduos foram empregadas umas argilas que são usadas na fabricação de materiais de cerâmica vermelha. Tanto os resíduos como as argilas tiveram sua composição mineralógica caracterizada por difração de raios X (DRX) e composição química por fluorescência de raios X (FRX). Esses resíduos foram misturados com argila e foram produzidas massas cerâmicas para avaliar seu desempenho nas propriedades fundamentais (resistência mecânica à flexão, densidade aparente, porosidade e absorção de água). Os corpos de prova foram conformados por prensagem uniaxial (25 MPa, 60×20×~4 mm³), e foram estudadas várias composições e duas temperaturas de queima (950°C e 1050°C), temperaturas usuais de queima em produtos de Cerâmica Vermelha. Alguns dos resultados obtidos cumprem com os parâmetros exigidos para a fabricação de diferentes tipos de produtos cerâmicos como tijolos, telhas e revestimentos cerâmicos.
Título en inglés
Reusability of red mud and sewage sludge as raw materials for ceramics.
Palabras clave en inglés
Ceramic materials
Recycling
Red mud
Sewage sludge
Resumen en inglés
Nowadays the environmental protection is an important matter. For that reason many companies are concerned about giving value to their residues, either to minimize operation costs or to sell raw material to other industries. With more restrictive legislation about wastes management, the traditional disposals are being rejected. Therefore, it is necessary to study new alternatives of final disposal and research new applications to transform industrial wastes into added-value products. This work aims to study the incorporation of two industrial wastes in ceramic materials; sewage sludge from a municipal wastewater treatment plant and red mud (a by-product of the Bayer process to produce alumina). In addition to those residues, it was used two local clays that are usually incorporated in ceramic bricks. Both residues as well as the clay were characterized by X-ray diffraction (XRD) and X-ray fluorescence (XRF). The residues and the clay were mixed, and prismatic probes were conformed to evaluate their technological properties (bending resistance, bulk density, porosity and water absorption). The ceramic probes were pressed uniaxially (25 MPa, 60×20×~4 mm³) and two temperatures (950°C and 1050°C), normally used in traditional ceramic industry, were studied. Some of the results fulfill the required parameters for the fabrication of different kinds of ceramic products as bricks, roof tiles and floor tiles.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-05-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.