Master's Dissertation
DOI
https://doi.org/10.11606/D.3.2014.tde-13082015-165238
Document
Author
Full name
Margarita Rosa Bobadilla Zimmermann
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2014
Supervisor
Committee
Tschiptschin, Andre Paulo (President)
Lima, Nelson Batista de
Pinedo, Carlos Eduardo
Title in Portuguese
Nitretação a plasma de um aço inoxidável duplex 2205.
Keywords in Portuguese
Aço inoxidável duplex
Difusão de nitrogênio
Nitretação a plasma
Abstract in Portuguese
Os aços inoxidáveis duplex se caracterizam por terem boas propriedades mecânicas e de resistência a corrosão, no entanto as suas propriedades de resistência ao desgaste são baixas. Para melhorar as propriedades superficiais desses materiais são utilizados tratamentos termoquímicos como a nitretação a plasma. Este tratamento é feito em temperaturas baixas para evitar a formação de nitretos de cromo, os quais quando são formados empobrecem o teor de cromo da matriz metálica, evitando que se forme a camada passiva, que confere resistência a corrosão a este tipo de material. Também, a nitretação a plasma permite que a dureza superficial atinja até dez vezes o valor da dureza inicial do material, o que melhora notavelmente as propriedades de resistência ao desgaste destes aços. Este estudo tem por objetivo avaliar camadas nitretadas formadas por nitretação a plasma em um aço inoxidável duplex AISI 2205. Para isto foram feitas várias experiências onde se estudou o efeito das variáveis do processo na formação da camada nitretada. Foram feitos tratamentos na temperatura de 400ºC sob pressões de 1,8 e 3,6 Torr por 720 min. Outra série de experimentos foi feita entre 350 e 500º por 240 min, para avaliar o efeito da temperatura nesse tratamento. Além disso, foi estudado o efeito de diferentes porcentagens de ferrita (40 e 64%) incialmente presente na microestrutura do material. Para isto foi feito um tratamento térmico de solubilização com têmpera em água a partir de 1200°C por uma hora, no material como recebido. A caracterização das camadas formadas foi feita por microscopia eletrônica de varredura, microscopia de força atômica, difração de raios x com radiação Cu K e difração de raios x de ângulo rasante a 5º. 7 Obtiveram-se camadas nitretadas com espessuras entre 3 µm e 18 µm. As espessuras das camadas sugerem que as variáveis: temperatura, tempo e pressão se relacionam com a espessura de forma direta, à medida que aumentam cada uma dessas variáveis, há um aumento da espessura da camada. As imagens obtidas por AFM sugerem que a nitretação a plasma induz mudanças na topografia da superfície, mudando com isto os valores de rugosidade. Também, foi observado que a espessura da camada nitretada é maior na amostra com menor percentagem de ferrita (40%). Nos difratogramas foi possível identificar a formação de austenita expandida e nitretos de cromo CrN.
Title in English
Pasma nitriding of a dupllex stainless steel 2005.
Keywords in English
Duplex stainless steel
Nitrogen diffusion
Plasma nitriding
Abstract in English
The duplex stainless steels are characterized by their good mechanical properties and corrosion resistance, but their wear resistance is low. To improve the surface properties of these materials plasma nitriding thermochemical treatments are used. This treatment is done at low temperatures to avoid chromium nitrides precipitation. CrN precipitation promotes the depletion of chromium of the metallic matrix preventing the formation of the chromium oxide layer that passivates these kind of materials. In addition, the plasma nitriding treatment allows reaching hardness values up to ten times greater the characteristic values of the untreated material, greatly improving the wear resistance of these steels. The aim of this work is to study nitrided layers formed by plasma nitriding in an AISI 2205 duplex stainless steel. For this, there were made several experiments where it was studied the effect of process variables on the nitrided layer formation. Treatments were performed at temperature of 400 °C under 1.8 and 3.6 Torr pressures during 720 min. Another series of experiments was tested between 350 °C and 500 °C during 240 min, to study the temperature effect. In addition, the effect of different ferrite percentages (40 and 64%) in the microstructure was studied. The ferrite percentage variation was obtained by a heat treatment of quenching in water at 1200 °C for one hour in the material as received. Samples characterization was done by scanning electron microscopy, atomic force microscopy and x-ray diffraction Cu K, glancing angle x-ray diffraction with an incident angle of 5º. There were obtained nitrided layer with a thickness between 3m and 18m. Layer thicknesses suggest that the variables: temperature, pressure and time are related to the thickness directly. AFM images obtained suggest that the plasma nitriding induces changes in surface topography, changing the values of roughness of the surface. In addition, it was observed that the layer thickness is bigger in the sample with less ferrite percentage (40%). X-ray patterns show the presence of expanded austenite and CrN.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2015-09-03
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.