Dissertação de Mestrado
DOI
10.11606/D.3.2016.tde-12072016-101827
Documento
Autor
Nome completo
Kleber Vaccioli
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2015
Orientador
Banca examinadora
Valera, Ticiane Sanches (Presidente)
Fechine, Guilhermino José Macêdo
Souza, Adriana Martinelli Catelli de
Título em português
Estudo da blenda PBAT/PLA com cargas.
Palavras-chave em português
Biodegradável
Blenda PBAT/PLA
Materiais compósitos
Polímeros (Materiais)
Resumo em português
Neste trabalho compósitos foram obtidos a partir da blenda comercial 100% biodegradável Ecovio® C2224 da BASF, uma blenda formada por 55% em massa de um copoliéster biodegradável, o Ecoflex® (poli[(adipato de butileno)-co-(tereftalato de butileno)]) e 45% em massa de PLA poli(ácido láctico). Como carga, utilizaram-se dois tipos de argilas comerciais do grupo das esmectitas, ambas predominantemente montmorilonitas: Cloisite Sódica® e Cloisite 30B®. Também foi utilizado como carga a sílica coloidal comercial Aerosil 200®, com área superficial de 200 m2/g e diâmetro médio de partícula 12nm. Os compósitos estudados, ambos contendo 5% e 10% em massa de cargas, foram preparados em uma extrusora de rosca dupla, acoplada a um reômetro de torque. O estudo foi dividido em três etapas: 1ª) etapa: Obtenção e caracterização dos compósitos de Ecovio®/ argila e Ecovio® / sílica; 2ª) etapa: Avaliação da fotodegradação do Ecovio® puro e dos compósitos obtidos; 3ª) etapa: Avaliação da biodegradabilidade do Ecovio® puro e dos compósitos após exposição em câmara de UV. As propriedades mecânicas dos compósitos antes e depois de serem submetidos à exposição em câmara de UV foram avaliadas por ensaios de resistência à tração e resistência ao impacto Izod. Os resultados obtidos na 1ª etapa deste trabalho indicaram aumento nos valores de módulo de elasticidade de todos os compósitos, em relação à blenda pura. Destacam-se as composições com 5% e 10% em massa de sílica coloidal, que apresentaram aumentos de até 115% nos valores de módulo de elasticidade, sem perdas significativas em resistência à tração, alongamento e resistência ao impacto, quando comparadas à fase matriz. Na 2ª etapa, a partir de 20 dias de exposição, todas as composições (blendas e compósitos) apresentam redução nas propriedades mecânicas em função do aumento do tempo de exposição à radiação UV. Na 3ª etapa, independente do tipo ou teor de carga presente na blenda, todas as composições apresentaram índices de biodegradabilidade, depois de 120 dias, de 40 a 60%, devido à prévia exposição à radiação UV.
Título em inglês
Study of PBAT/PLA blend with filler.
Palavras-chave em inglês
Biodegradable
Composite
PBAT / PLA blend
Resumo em inglês
In this work, composites were prepared with 100% biodegradable commercial blend Ecovio® C2224 BASF, a polymer blend composed of 55 wt% of a biodegradable copolyester, the Ecoflex®, poly [(butylene adipate) -co- (butylene terephthalate)], and 45 wt% of PLA poly(lactic acid). Two types of commercial clays of the smectite group, predominantly montmorillonites, were used as fillers: Cloisite Na+® and Cloisite 30B®. The commercial colloidal silica Aerosil 200®, with a surface area of 200 m2/g and an average particle diameter of 12 nm, was also used as filler. The composites containing 5 and 10 wt% of filler were obtained in a twin screw extruder coupled to a torque rheometer. This study was divided in three steps: 1st) Preparation and characterization of Ecovio®/clay and Ecovio®/silica composites; 2nd) Evaluation of the photodegradation of pure Ecovio® and of the composites; 3rd) Biodegradability assessment of pure Ecovio® and composites after exposure to UV chamber. The mechanical properties of the composites before and after the exposition to UV were evaluated by tensile and Izod impact strength. The results obtained in the 1st step showed an increase in the tensile modulus of all blends, especially for the compositions with 5 and 10 wt% of colloidal silica, which presented an increase of 115% in their tensile modulus values without significant reduction in impact and tensile strength and elongation, when compared to the pure blend. In the 2nd step, from 20 UV exposure days, all compositions (blends and composites), presented a significant reduction in the mechanical properties as a function of the increase of the UV radiation exposure time. In step 3, regardless of the filler type or content, all blend compositions showed biodegradability index, after 120 days, of 40 to 60%, due to the prior UV exposure.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2016-07-13
 
AVISO: O material descrito abaixo refere-se a trabalhos decorrentes desta tese ou dissertação. O conteúdo desses trabalhos é de inteira responsabilidade do autor da tese ou dissertação.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2022. Todos os direitos reservados.