Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.3.1994.tde-12042022-133853
Document
Auteur
Nom complet
Claudio Geraldo Schön
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 1994
Directeur
Jury
Goldenstein, Helio (Président)
Landgraf, Fernando Jose Gomes
Rechenberg, Hercilio Rodolfo
Titre en portugais
Estudo microestrutural da austenita de uma liga de ferro contendo 8% de cromo e 1,2% de carbono.
Mots-clés en portugais
Aço
Carbono
Materiais
Resumé en portugais
Austenitas encontradas em aços são comumente descritas como soluções sólidas homogêneas desordenadas. Um estudo recente, entretanto, iniciou que esta imagem não é correta para o sistema 'Fe'-'Cr'- C, de grande importância tecnológica. No presente trabalho, as técnicas de difração de nêutrons em amostra policristalina e espectroscopia Mossbauer por elétrons de conversão foram empregadas para investigar a estrutura ordenada da austenita de uma liga 'Fe'-8%'Cr'-1,2% C solubilizada a 1473 kelvin durante 200 horas. Os resultados confirmam a distribuição do cromo segundo um supereticulado de estequiometria ferro sete cromo. Quanto ao carbono, os resultados contradizem a sua distribuição nos interstícios octaédricos do supereticulado, embora a análise do espectro Mossbauer indique forte repulsão entre os intersticiais e sua concentração na vizinhança dos átomos de cromo. Estes resultados são compatíveis com uma distribuição ordenada a longo alcance tanto do cromo quanto do carbono nesta liga.
Titre en anglais
Microstructural study of the austenite in an iron, 8wt% chromium, 1,2wt%.
Mots-clés en anglais
Carbon
Materials
Steel
Resumé en anglais
Microstructural study of the austenite in an iron, 8wt% chromium, 1.2 wt% carbon alloy. Steel austenites are usually described as homogeneous disordered solid solutions. A recent study indicates, however, that this picture is no longer valid for the technologically important Fe-Cr-C system. In this work, neutron powder diffraction and conversion electron Mössbauer spectroscopy were used to investigate the ordered structure of an Fe-8wt%cr-1.2wt%C austenite. The results confirm the distribution of chromium in an 7 chromium stoichiometry superlattice. The carbon distribution does not agree with an octahedral interstitial occupancy, although the Mössbauer spectrum analysis indicates a strong repulsion between interstitials and an enrichment of the neighbourhood of chromium with carbon. These results are compatible with long-range order both of chromium atoms and of carbon atoms.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2022-04-12
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.