Disertación de Maestría
DOI
https://doi.org/10.11606/D.3.1994.tde-12042022-133853
Documento
Autor
Nombre completo
Claudio Geraldo Schön
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1994
Director
Tribunal
Goldenstein, Helio (Presidente)
Landgraf, Fernando Jose Gomes
Rechenberg, Hercilio Rodolfo
Título en portugués
Estudo microestrutural da austenita de uma liga de ferro contendo 8% de cromo e 1,2% de carbono.
Palabras clave en portugués
Aço
Carbono
Materiais
Resumen en portugués
Austenitas encontradas em aços são comumente descritas como soluções sólidas homogêneas desordenadas. Um estudo recente, entretanto, iniciou que esta imagem não é correta para o sistema 'Fe'-'Cr'- C, de grande importância tecnológica. No presente trabalho, as técnicas de difração de nêutrons em amostra policristalina e espectroscopia Mossbauer por elétrons de conversão foram empregadas para investigar a estrutura ordenada da austenita de uma liga 'Fe'-8%'Cr'-1,2% C solubilizada a 1473 kelvin durante 200 horas. Os resultados confirmam a distribuição do cromo segundo um supereticulado de estequiometria ferro sete cromo. Quanto ao carbono, os resultados contradizem a sua distribuição nos interstícios octaédricos do supereticulado, embora a análise do espectro Mossbauer indique forte repulsão entre os intersticiais e sua concentração na vizinhança dos átomos de cromo. Estes resultados são compatíveis com uma distribuição ordenada a longo alcance tanto do cromo quanto do carbono nesta liga.
Título en inglés
Microstructural study of the austenite in an iron, 8wt% chromium, 1,2wt%.
Palabras clave en inglés
Carbon
Materials
Steel
Resumen en inglés
Microstructural study of the austenite in an iron, 8wt% chromium, 1.2 wt% carbon alloy. Steel austenites are usually described as homogeneous disordered solid solutions. A recent study indicates, however, that this picture is no longer valid for the technologically important Fe-Cr-C system. In this work, neutron powder diffraction and conversion electron Mössbauer spectroscopy were used to investigate the ordered structure of an Fe-8wt%cr-1.2wt%C austenite. The results confirm the distribution of chromium in an 7 chromium stoichiometry superlattice. The carbon distribution does not agree with an octahedral interstitial occupancy, although the Mössbauer spectrum analysis indicates a strong repulsion between interstitials and an enrichment of the neighbourhood of chromium with carbon. These results are compatible with long-range order both of chromium atoms and of carbon atoms.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2022-04-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.