Disertación de Maestría
DOI
10.11606/D.3.2011.tde-12032012-121409
Documento
Autor
Nombre completo
Erick Renato Vargas Garcia
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2011
Director
Tribunal
Brandi, Sérgio Duarte (Presidente)
Machado, Izabel Fernanda
Poetscher, Freddy
Título en portugués
Efeito da corrente de soldagem do processo TIG pulsado autógeno na microestrutura da zona fundida dos aços inoxidáveis duplex UNS S32304 e UNS S32101.
Palabras clave en portugués
Soldagem autógena
Soldagem dos aços inoxidáveis duplex baixa liga
TIG
Resumen en portugués
A microestrutura e a composição química dos aços inoxidáveis duplex são responsáveis pela sua resistência mecânica e sua resistência à corrosão que, geralmente, é superior aos aços inoxidáveis ferríticos e austeníticos convencionais. A soldagem destes materiais causa tanto alteração de microestrutura como de composição química, que podem ser alteradas dependendo dos processos de soldagem, dos parâmetros de soldagem, da utilização ou não de metal de adição e da composição química do gás de proteção, nos processos que utilizam proteção gasosa. No caso dos aços inoxidáveis duplex baixa liga, a solidificação é completamente ferrítica, podendo produzir tamanho de grão exagerado no metal de solda e na ZAC. O objetivo deste trabalho é de avaliar o efeito da freqüência de pulsação do processo TIG autógeno na soldagem de aços inoxidáveis duplex baixa liga. Foram soldadas chapas de aços inoxidáveis duplex baixa liga UNS S32304 e UNS S32101 (lean duplex), sem metal de adição e empregando-se argônio como gás de proteção. A soldagem foi executada com o processo TIG, mantendo-se a energia de soldagem constante, de 340 J/mm, e variando-se a freqüência de pulsação entre 1, 5, 10 e 20 Hz. As microestruturas resultantes tanto no metal de solda, região central e região sem mistura, bem como na zona afetada pelo calor foram caracterizadas através de microscopia ótica. Os resultados mostraram que, na soldagem autógena, independente de ter ou não a pulsação da corrente, ocorre um aumento no tamanho do grão da zona fundida devido a solidificação ferrítica deste aço. Comparando-se os resultados do tamanho do grão e da fração volumétrica de ferrita no metal de solda, notouse um aumento no tamanho de grão e na fração volumétrica da ferrita com o aumento da freqüência de pulsação.
Título en inglés
Effect of the welding current of the process TIG pulsed without the addition of filler metal in the microestructure of the fusion zone of the duplex stainless steel UNS S32304 and UNS S32101.
Palabras clave en inglés
Duplex stainless steel
Gtaw
Weldability of duplex stainless steel
Resumen en inglés
The microstructure and chemical composition of duplex stainless steel are responsible for their mechanical strength and corrosion resistance. The welding of these materials produces a change in the microstructure and chemical composition. These changes depend on: welding processes, welding parameters, the use or absence of filler metal and composition of shielding gas in processes that use shielding gas. In the case of lean duplex stainless steel the solidification is fully ferritic, which may produce an excessive grain size in the weld metal and in the heat affected zone (HAZ). The main goal of this paper is to evaluate the effect of pulse frequency in autogenous TIG welding process of lean duplex stainless steel. In this sense, plates of UNS S32304 and UNS S32101 lean duplex were welded without filler metal and using argon as shielding gas. The welds were made using the GTAW process, keeping the heat input constant at 340 J/mm and varying the pulse frequency between 1,5,10 and 20 Hz. The results showed that, independent of pulse frequency, grain growth in the fusion zone took place since this duplex stainless steel type has a ferritic solidification mode. Comparing the grain size and ferrite volumetric fraction in the weld bead, an increase in the mean value of grain size in the central region and unmixed region of weld beads was related to an increase of pulse frequency.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-04-05
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.