Disertación de Maestría
DOI
10.11606/D.3.2008.tde-10102008-061334
Documento
Autor
Nombre completo
Caio Fazzioli Tavares
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Padilha, Angelo Fernando (Presidente)
Martorano, Marcelo de Aquino
Rossi, Jesualdo Luiz
Título en portugués
Influência da composição química e da espessura da peça fundida na quantidade e distribuição de ferrita delta em aços inoxidáveis austeníticos.
Palabras clave en portugués
Aço inoxidável austenítico
Composição química
Fundição de ferrosos
Resumen en portugués
Os aços inoxidáveis possuem numerosas aplicações devido à boa combinação de propriedades tais como resistência à corrosão e oxidação, ductilidade, tenacidade, soldabilidade e resistência mecânica em temperaturas elevadas. No entanto suas propriedades e desempenho estão fortemente relacionados com a microestrutura que por sua vez, no caso de peças fundidas, dependem principalmente da composição química e da velocidade de solidificação. No presente trabalho o efeito destas duas variáveis foram estudados e os resultados experimentais comparados com as previsões teóricas e modelos disponíveis na literatura. Dezesseis corridas de diferentes aços inoxidáveis austeníticos foram fundidas e suas composições químicas completas (16 elementos analisados) foram determinadas. A maioria das corridas analisadas apresentou modo de solidificação do tipo C. Foram encontrados teores de ferrita (medidos com auxílio de ferritoscopia) na faixa de 0 a 11%. A influência da composição química do aço na quantidade de ferrita delta formada foi marcante, enquanto a influência da espessura foi pouco acentuada. Dentre as numerosas fórmulas testadas para a previsão da quantidade de ferrita delta, as duas que apresentaram melhor resultado foram as fórmulas de Schneider e de Schoefer, sendo que esta última é recomendada pela norma ASTM A800. A amostra contendo cerca de 10% de ferrita apresentou uma rede quase contínua, o que pode comprometer a tenacidade da peça, caso esta ferrita venha a sofrer fragilização. Nas amostras contendo por volta de 5% de ferrita, a rede de ferrita é semi-contínua, enquanto para teores baixos (por volta de 2%), a ferrita apresenta-se como ilhas isoladas. As morfologias encontradas foram classificadas como sendo todas do tipo vermicular. Os estudos de micro-análise química dos elementos Si, Mo, Cr, Fe e Ni, efetuados na ferrita e na austenita revelaram coeficientes de partição de acordo com o previsto pela literatura. O efeito da espessura nas variações de composição foi pequeno e não conclusivo.
Título en inglés
Chemical composition and casting thikness influence on delta ferrite quantity and distibution in austenitic stainless steels.
Palabras clave en inglés
Austenitic stainless steel
Delta ferrite
Microstructure
Solidification
Resumen en inglés
Stainless steel has numerous applications due to a good combination of properties such as corrosion and oxidation resistance, toughness, weldability and mechanical strength at high temperatures. However these properties and performance are strongly related to the microstructure and in the case of castings are mainly dependent of chemical composition and cooling rate. In this work the effect of these two factors were studied and the experimental results compared with theoretical models available in the literature. Sixteen heats of different austenitic stainless steel were cast and their complete chemical compositions (16 elements) were determined. Most of analyzed heats showed the solidification mode type C. Ferrite values (measured with ferritoscope) were found in the range from 0 to 11%. The influence of chemical composition on delta ferrite was strong while the influence of thickness was less accentuated. Among numerous tested formulas to estimate the quantity of delta ferrite two that demonstrated better results were the ones of Schneider and Schoefer, where the last one is recommended by ASTM A800 standard. The sample with approximately 10% of ferrite showed an almost continuous ferrite network microstructure that may deteriorate component part toughness if this ferrite comes to suffer embrittlement. On the samples with content ferrite around 5% the ferrite network is semi-continuous while for low values (around 2%) the ferrite showed isolated cores. The morphologies were classified as vermicular. The study of micro chemical analysis of Si, Mo, Cr, Fe and Ni on ferrite and austenite showed partition coefficient in accordance with values defined in literature. The thickness effect on chemical composition was small and not conclusive.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
PMTedrev_CFTAVARES.pdf (10.05 Kbytes)
Fecha de Publicación
2009-10-09
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • Martorano, Marcelo Aquino, Tavares, Caio Fazzioli, and Padilha, Angelo Fernando. Predicting Delta Ferrite Content in Stainless Steel Castings [doi:10.2355/isijinternational.52.1054]. ISIJ International [online], 2012, vol. 52, p. 1054-1065.
  • Padilha, Angelo Fernando, Tavares, Caio Fazzioli, e Martorano, Marcelo Aquino. Delta Ferrite Formation in Austenitic Stainless Steel Castings [doi:10.4028/www.scientific.net/msf.730-732.733]. Materials Science Forum [online], 2012, vol. 730-732, p. 733-738.