Disertación de Maestría
DOI
10.11606/D.3.2018.tde-10042018-134754
Documento
Autor
Nombre completo
Saul Hissaci de Souza
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2018
Director
Tribunal
Padilha, Angelo Fernando (Presidente)
Fernandes, Ricardo do Carmo
Lima, Nelson Batista de
Título en portugués
Cinética de amolecimento da liga de alumí­nio AA 7075 durante recozimento após laminação a frio.
Palabras clave en portugués
Alumínio
Ligas leves
Recristalização
Resumen en portugués
O presente trabalho apresenta um estudo sobre o amolecimento após laminação e recozimento da AA 7075, uma liga de alumínio endurecível por precipitação . As amostras recebidas no estado T6 foram caracterizadas com auxílio das técnicas de microscopia óptica de luz polarizada, microscopia eletrônica de varredura, espectroscopia de raios X por dispersão de energia, difração de raios X, condutividade elétrica e dureza Vickers . As amostras foram então separadas em dois grupos. O primeiro sofreu um tratamento térmico de solubilização (485°C por 5 horas) enquanto o segundo foi submetido a um tratamento de superenvelhecimento (300°C por 5 horas) e, em seguida, ambos os grupos de amostras tratadas foram novamente caracterizadas pelas técnicas descritas anteriormente (exceto microscopia óptica) e laminadas a frio. Durante a etapa de laminação, constatou-se a dificuldade em causar deformação plástica na amostra solubilizada. Optou-se em conduzir o estudo com as amostras superenvelhecidas, que foram laminadas com reduções de 45%, 75% e 90% em espessura. A seguir, estas foram submetidas a tratamentos isotérmicos e isócronos com o objetivo de estudar a cinética de amolecimento das amostras deformadas a frio. As amostras superenvelhecidas e deformadas em 45% em redução de espessura, apresentaram somente indícios de início de recristalização (nas amostras tratadas a partir de 250°C por 1 hora) via EBSD, sendo que a maior parte do amolecimento pode ser explicada pelo mecanismo de recuperação. Além disso, a cinética de amolecimento das amostras recozidas nesse grupo apresentaram boa concordância com a lei logarítmica proposta por Kulhmann (1948) e (coincidentemente) também com o consolidado modelo JMAK. As amostras superenvelhecidas e deformadas em 75% e 90% apresentaram comportamento similar (isso é, principalmente recuperação) para recozimentos realizados em temperaturas de até 350°C por uma hora. Recozimentos realizados a 400°C promoveram a recristalização total das amostras desse grupo para tempos inferiores a 15 minutos. Dessa forma, não foi possível estudar a cinética de recristalização para esse segundo grupo de amostras.
Título en inglés
Softening behavior during annealing of col-rolled aluminium alloy 7075.
Palabras clave en inglés
AA 7075
Aluminium alloys
Recovering
Recrystallization
Resumen en inglés
This work presents a study about the softening after cold rolling and annealing of aluminium alloy AA 7075. Firstly, polarized light optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, electrical conductivity and Vickers hardness have been used at the starting material (T6). The samples were then separated in two groups. The former underwent a solubilization heat treatment (485°C for 5 hours) whilst the latter underwent an overaging treatment to grow up the existing precipitates (300°C for 5 hours). Both groups of treated samples were again characterized by the techniques described above (except optical microscopy). In the rolling stage, the difficulty in straining the solubilized sample and the relative ease for doing so to the overaged sample was verified. It was therefore decided to conduct the study with the samples of the second group, which were 45%, 75% and 90% rolled in thickness reduction. Then, they underwent isothermal and isochronous treatments in order to study its softening kinetics by Vickers hardness measurements, polarized light optic microscopy and EBSD. The overaged and rolled samples (45% in thickness reduction) didn't present evidences of recrystallization except by very few grains found via EBSD (in samples treated from 250 ° C for 1 hour). So, most of the observed softening can be explained by recovery. In addition, the softening kinetics of the annealed samples in this group showed good agreement with the logarithmic law proposed by Kulhmann (1948) and (coincidentally) also with the consolidated JMAK model. The overaged samples that underwent thickness reduction of 75% and 90% showed a similar behavior (that is, mainly recovery) for annealing at temperatures up to 350 ° C. Annealing at 400 ° C promoted total recrystallization of the samples from this group (75% and 90% in thickness reduction) in less than 15 minutes. Thus, it was not possible to study the kinetics of recrystallization for this second group of samples.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-04-10
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.