Tesis Doctoral
DOI
10.11606/T.3.2017.tde-07112017-145922
Documento
Autor
Nombre completo
Marcos Gonzales Fernandes
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2017
Director
Tribunal
Wiebeck, Hélio (Presidente)
Cortés, Guillermo Ruperto Martín
Diaz, Francisco Rolando Valenzuela
Esper, Fábio José
Silva, Leonardo Gondim de Andrade e
Título en portugués
Obtenção de nanocompósitos de borracha natural e organoargila com variação no processo de organofilização.
Palabras clave en portugués
Argilas
Borracha
Nanocompósitos
Resumen en portugués
Foi preparado o nanocompósito de borracha natural/argila chocolate B modificada por sodificação via seca com variação no processo, utilizando silicato de sódio ao invés de carbonato de sódio e tratada com sal quaternário de amônio, cloreto hexadecil trimetil amônio. A argila no seu estado natural, após sodificação e após quaternização foi caracterizada pelas técnicas de microscopia estereoscópica, análise térmica, infravermelho, difração de raios X e microscopia eletrônica de varredura. Outras cargas orgânicas foram adicionadas, como celulose e piaçava e comparadas com cargas tradicionais, como o negro de fumo. As placas obtidas, após vulcanização, tiveram medidas as suas propriedades mecânicas e foram analisadas por DRX e MEV. Os nanocompósitos obtidos mostraram melhoria nas suas propriedades mecânicas em comparação com as placas sem a adição de argila.
Título en inglés
Making natural rubber-organoclay nanocompósites with variation in the organophilization process.
Palabras clave en inglés
Nanocomposites
Natural rubber
Natural rubber nanocomposites
Organophilic clays
Resumen en inglés
The natural rubber/clay chocolate B nanocomposite modified by dry sodification process with variation processing was prepared using sodium silicate instead of sodium carbonate and treated with quaternary ammonium salt, hexadecyl trimethyl ammonium chloride. The clay in its natural state after sodification and after quaternization was characterized by the techniques of stereoscopic microscopy, thermal analysis, infrared, X-ray diffraction and scanning electron microscopy. Other organic fillers were added, such as cellulose and piaçava, and compared with traditional fillers such as carbon black. The plates obtained after vulcanization had their mechanical properties measured and were analyzed by XRD and SEM. The obtained nanocomposites showed improvement in their mechanical properties in comparison with the plates without the addition of clay.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-11-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.