Tesis Doctoral
DOI
10.11606/T.3.2007.tde-06072007-143145
Documento
Autor
Nombre completo
Isabella Marini Vargas
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2007
Director
Tribunal
Wiebeck, Hélio (Presidente)
Kawano, Yoshio
Silva, Leonardo Gondim de Andrade e
Valenzuela Díaz, Francisco Rolando
Valera, Ticiane Sanches
Título en portugués
Reciclagem de vidro laminado: utilização na fabricação de isolantes e vernizes com alta resistência à abrasão para pisos de madeira.
Palabras clave en portugués
Abrasão
Materiais isolantes
Resíduos industriais (reciclagem)
Resistência dos materiais
Vernizes e lacas
Resumen en portugués
Neste trabalho apresenta-se uma alternativa para utilização de vidros laminados provenientes de rejeitos industriais ou pós-consumo. Reciclando o vidro laminado, por meio de uma série de moagens, pode-se obter dois tipos de rejeitos: vidros de partículas pequenas (200 e 325 mesh), que não conseguem ser reaproveitados pela indústria vidreira, e filme de poli(vinil butiral) - PVB - impregnado com uma pequena quantidade de carga, que tem como destino os aterros. No presente estudo, esses dois resíduos foram aproveitados na fabricação de vernizes curados por radiação ultravioleta empregados para proteção de pisos de madeira. O filme de PVB foi utilizado na formulação de um isolante, em razão de sua alta flexibilidade e boa aderência à madeira, e o vidro de baixa granulometria foi empregado como carga nos vernizes chamados de alto tráfego para o aumento da resistência à abrasão dos mesmos (propriedade fundamental de vernizes para pisos de madeira). Pelos resultados obtidos, verificou-se que o isolante preparado com o filme de PVB em solução alcoólica e misturado a um monômero acrílico trifuncional, como o trimetilolpropano triacrilato (TMPTA), quando aplicado sobre pisos de madeira, obteve-se bons resultados de aderência, arrancamento e flexibilidade, podendo assim substituir os isolantes utilizados atualmente, produtos com cura por radiação ultravioleta, em base aquosa, e que apresentam alto custo por serem preparados com resinas importadas. Foi observado que quanto maior a quantidade de solução de PVB, melhor a flexibilidade do filme e, conseqüentemente, melhor a resistência ao arrancamento do revestimento. Os vidros de baixa granulometria apresentaram resultados muito satisfatórios quando utilizados como carga nos vernizes de alto tráfego, especialmente ao se combinarem com o óxido de alumínio (carga atualmente utilizada nesses sistemas), aumentando ainda mais a resistência à abrasão dos vernizes e também a estabilidade dos vernizes (quanto à sedimentação e à geleificação). Para todas as combinações de cargas preparadas neste trabalho foram bons os resultados obtidos, podendo-se optar pela utilização daquelas com maior quantidade de vidro, uma vez que este, por tratar-se de um resíduo, torna tais combinações mais econômicas.
Título en inglés
Windshield recycling: in the fabrication of isolators and varnishes with high abrasion resistance for wood flooring.
Palabras clave en inglés
Abrasion
Industrial residues (recycling)
Isolator materials
Materials resistance
Varnishes
Resumen en inglés
The present work features an alternative for the utilization of the windshield after its use. The recycling of the laminated glass, through a series of grindings, make possible to obtain two kinds of materials: glasses of small particles (200 and 325 mesh), that cannot be recovered in the glass industry, and a poly(vinyl butiral) - PVB - sheet impregnated with a small amount of filler, that has as final disposal the sanitary landfill. In this study these two materials were introduced in the formulation of ultraviolet curing varnishes used to the protection of wood flooring. The film of PVB was used in the formulation of a primer, due to its high flexibility and good adherence to the wood, and the glass of low granulometry was used as a filler in the so-called high traffic varnish, to increase the abrasion resistance (main property of these varnishes). The results obtained showed that the primer prepared with the PVB sheet in alcoholic solution, mixed with a trifunctional acrylic monomer, like TMPTA, when applied on wood flooring, obtained good results of adherence, scrape adhesion, flexibility and stability and could substitute the primers used nowadays that are UV curing products, however water based ones, and that has a high cost because of the imported resins that are used in their formulations. It was observed that larger the amount of solution of PVB, better the flexibility of the film and, consequently, better its scrape adhesion. The glasses of low granulometry also presented very satisfactory results when used as fillers in the high traffic varnishes, mainly when in combination with aluminium oxide (filler used in these systems), increasing more the abrasion resistance of the varnishes and also their stability (the sedimentation and geleification have showed better results). To all filler combinations studied in this work the results were good and the best one can be the ones that presented the largest amount of glass, since as a residue, make these combinations more economical.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
significa que el fichero sólamente puede ser acceder dentro da la Universidad de São Paulo.
Fecha de Publicación
2007-08-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.