Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.3.2018.tde-05032018-152845
Document
Auteur
Nom complet
Roberto Silva de Andrade
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2017
Directeur
Jury
Mourão, Marcelo Breda (Président)
Moraes, Sandra Lúcia de
Júnior, Ramiro da Conceição do Nascimento
Titre en portugais
Efeito da basicidade e do teor de MgO no inchamento de pelotas de minério de ferro.
Mots-clés en portugais
Ferro
Inchamento
Minérios
Pelotização
Resistência dos materiais
Resumé en portugais
O inchamento de pelotas de minério de ferro, que pode chegar até 400%, é um assunto que desperta interesse da indústria metalúrgica por gerar diversos problemas durante processos de redução. Ele ocorre por dois motivos, a saber, a mudança da estrutura cristalina na transformação da hematita (Fe2O3) para a magnetita (Fe3O4) e o aparecimento de ferro no formato filamentar durante a última etapa de redução. Diversos fatores influenciam o comportamento das pelotas, como a basicidade binária (CaO/SiO2) e o teor de MgO. Foram realizados experimentos para avaliar o efeito destas duas variáveis em suas propriedades físicas, como resistência à compressão e porosidade, e no comportamento das pelotas durante a redução. Os teores de MgO foram de 0%, 1% e 5%, enquanto a basicidade foi de 0,61 a 1,5. Ao adicionar MgO, a porosidade e a redutibilidade aumentam, enquanto o inchamento e a resistência diminuem. Ao adicionar CaO, a porosidade cai por conta da formação de mais fase líquida durante a queima, há diminuição de inchamento. A redutibilidade aumenta até basicidade 1 e depois apresenta uma leve diminuição em basicidade 1,5.
Titre en anglais
Effect of basicity and MgO content in the swelling of iron ore pellets.
Mots-clés en anglais
Iron ore
Pelletizing
Reduction
Swelling
Resumé en anglais
Iron ore pellets swelling, which can reach up to 400%, is a subject that rises concern in metallurgical industry because of the problems it may cause during reduction processes. Several factors can change pellets behavior concerning swelling, such as binary basicity (CaO/SiO2) and the MgO content. Experiments were performed to evaluate the effect of these two variables in the physical properties of the pellets, such as compression strength and porosity, and in their behavior during reduction as well. MgO was added up to 5% and basicity varied in a range from 0.61 to 1.5. Addition of MgO increased porosity and reducibility, while swelling and strength decreased. Addition of CaO caused porosity to decrease because of the formation of more liquid slag during heat treatment. Is also decreased swelling. Reducibility rises when basicity reaches 1.0, but decreases with further increases in CaO content.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2018-03-09
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.