Disertación de Maestría
DOI
10.11606/D.3.2018.tde-05032018-152845
Documento
Autor
Nombre completo
Roberto Silva de Andrade
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2017
Director
Tribunal
Mourão, Marcelo Breda (Presidente)
Moraes, Sandra Lúcia de
Júnior, Ramiro da Conceição do Nascimento
Título en portugués
Efeito da basicidade e do teor de MgO no inchamento de pelotas de minério de ferro.
Palabras clave en portugués
Ferro
Inchamento
Minérios
Pelotização
Resistência dos materiais
Resumen en portugués
O inchamento de pelotas de minério de ferro, que pode chegar até 400%, é um assunto que desperta interesse da indústria metalúrgica por gerar diversos problemas durante processos de redução. Ele ocorre por dois motivos, a saber, a mudança da estrutura cristalina na transformação da hematita (Fe2O3) para a magnetita (Fe3O4) e o aparecimento de ferro no formato filamentar durante a última etapa de redução. Diversos fatores influenciam o comportamento das pelotas, como a basicidade binária (CaO/SiO2) e o teor de MgO. Foram realizados experimentos para avaliar o efeito destas duas variáveis em suas propriedades físicas, como resistência à compressão e porosidade, e no comportamento das pelotas durante a redução. Os teores de MgO foram de 0%, 1% e 5%, enquanto a basicidade foi de 0,61 a 1,5. Ao adicionar MgO, a porosidade e a redutibilidade aumentam, enquanto o inchamento e a resistência diminuem. Ao adicionar CaO, a porosidade cai por conta da formação de mais fase líquida durante a queima, há diminuição de inchamento. A redutibilidade aumenta até basicidade 1 e depois apresenta uma leve diminuição em basicidade 1,5.
Título en inglés
Effect of basicity and MgO content in the swelling of iron ore pellets.
Palabras clave en inglés
Iron ore
Pelletizing
Reduction
Swelling
Resumen en inglés
Iron ore pellets swelling, which can reach up to 400%, is a subject that rises concern in metallurgical industry because of the problems it may cause during reduction processes. Several factors can change pellets behavior concerning swelling, such as binary basicity (CaO/SiO2) and the MgO content. Experiments were performed to evaluate the effect of these two variables in the physical properties of the pellets, such as compression strength and porosity, and in their behavior during reduction as well. MgO was added up to 5% and basicity varied in a range from 0.61 to 1.5. Addition of MgO increased porosity and reducibility, while swelling and strength decreased. Addition of CaO caused porosity to decrease because of the formation of more liquid slag during heat treatment. Is also decreased swelling. Reducibility rises when basicity reaches 1.0, but decreases with further increases in CaO content.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-03-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.