Master's Dissertation
DOI
10.11606/D.3.2018.tde-05032018-152845
Document
Author
Full name
Roberto Silva de Andrade
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2017
Supervisor
Committee
Mourão, Marcelo Breda (President)
Moraes, Sandra Lúcia de
Júnior, Ramiro da Conceição do Nascimento
Title in Portuguese
Efeito da basicidade e do teor de MgO no inchamento de pelotas de minério de ferro.
Keywords in Portuguese
Ferro
Inchamento
Minérios
Pelotização
Resistência dos materiais
Abstract in Portuguese
O inchamento de pelotas de minério de ferro, que pode chegar até 400%, é um assunto que desperta interesse da indústria metalúrgica por gerar diversos problemas durante processos de redução. Ele ocorre por dois motivos, a saber, a mudança da estrutura cristalina na transformação da hematita (Fe2O3) para a magnetita (Fe3O4) e o aparecimento de ferro no formato filamentar durante a última etapa de redução. Diversos fatores influenciam o comportamento das pelotas, como a basicidade binária (CaO/SiO2) e o teor de MgO. Foram realizados experimentos para avaliar o efeito destas duas variáveis em suas propriedades físicas, como resistência à compressão e porosidade, e no comportamento das pelotas durante a redução. Os teores de MgO foram de 0%, 1% e 5%, enquanto a basicidade foi de 0,61 a 1,5. Ao adicionar MgO, a porosidade e a redutibilidade aumentam, enquanto o inchamento e a resistência diminuem. Ao adicionar CaO, a porosidade cai por conta da formação de mais fase líquida durante a queima, há diminuição de inchamento. A redutibilidade aumenta até basicidade 1 e depois apresenta uma leve diminuição em basicidade 1,5.
Title in English
Effect of basicity and MgO content in the swelling of iron ore pellets.
Keywords in English
Iron ore
Pelletizing
Reduction
Swelling
Abstract in English
Iron ore pellets swelling, which can reach up to 400%, is a subject that rises concern in metallurgical industry because of the problems it may cause during reduction processes. Several factors can change pellets behavior concerning swelling, such as binary basicity (CaO/SiO2) and the MgO content. Experiments were performed to evaluate the effect of these two variables in the physical properties of the pellets, such as compression strength and porosity, and in their behavior during reduction as well. MgO was added up to 5% and basicity varied in a range from 0.61 to 1.5. Addition of MgO increased porosity and reducibility, while swelling and strength decreased. Addition of CaO caused porosity to decrease because of the formation of more liquid slag during heat treatment. Is also decreased swelling. Reducibility rises when basicity reaches 1.0, but decreases with further increases in CaO content.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2018-03-09
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2022. All rights reserved.