Encruamento e recristalização dos aços inoxidáveis EUROFER e ODS-EUROFER para aplicação em reatores de fusão nuclear.
Mots-clés en portugais
Engenharia metalúrgica
Ensaios da estrutura dos materiais
Materiais nucleares
Resumé en portugais
Este trabalho consiste em uma pesquisa sobre aços inoxidáveis ferríticomartensíticos de ativação reduzida (RAFM): EUROFER (9Cr-1W) e ODS-EUROFER (9Cr-1W-0,3Y2O3), envolvendo o encruamento e a recristalização destas duas ligas com o objetivo de estudar a influência de uma dispersão de partículas nanométricas na recristalização de aços inoxidáveis. O conceito de materiais de ativação reduzida é discutido e é apresentada a aplicação destes aços tanto na estrutura de diversor do ITER quanto na primeira parede no módulo de câmara fértil do reator DEMO. As placas, no estado revenido, foram laminadas a frio em um laminador de pequeno porte. As curvas de encruamento de ambos os materiais mostram um comportamento quase linear. Os tratamentos isócronos de uma hora, entre 300 e 750 °C, resultaram curvas de amolecimento que indicam uma forte resistência à recristalização da liga ODS-EUROFER, em concordância com os modelos teóricos. A liga EUROFER-97 apresentou recristalização muito similar a liga comercial 430, mas com maior dureza inicial, devido a maior quantidade de elementos intersticiais.
Titre en anglais
Work hardening and recrystallization of EUROFER and ODS-EUROFER stainless steels to nuclear fusion reactors application.
Mots-clés en anglais
Materials structure testing
Metallurgical engineering
Nuclear materials
Resumé en anglais
This work studies reduced activation ferritic-martensitic (RAFM) stainless steels: EUROFER (9Cr-1W) and ODS-EUROFER (9Cr-1W-0,3Y2O3), and their work hardening and recrystallization behaviour to better understand the influence of a dispersion of nanometric particles on the recrystallization process of stainless steels. The concept of reduced activation materials is discussed and the application of these steel alloys, such as in the divertor structure of ITER (International Thermonuclear Experimental Reactor) and as in the DEMO reactor breeding blanket first wall is shown. The plates, in the as-tempered condition, were cold rolled in a laboratory rolling mill. The work hardness curves of both materials presented an approximately linear behavior with strain increase. One hour isochronal treatments, in the temperature range from 300 to 750 °C, resulted in softening curves that indicated a strong resistance to recrystallization of the alloy ODS-EUROFER, supporting the theorical models. The EUROFER-97 recrystallization showed a similar behaviour to the commercial 430 alloy, however with higher initial hardness, due to the larger amount of interstitial elements.
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2010-05-24
AVERTISSEMENT: Le matériau se réfère à des documents provenant de cette thèse ou mémoire. Le contenu de ces documents est la responsabilité de l'auteur de la thèse ou mémoire.
- TERADA, Maysa, et al. Corrosion behavior of Eurofer 97 and ODS-Eurofer alloys compared to traditional stainless steels [doi:10.1007/s10800-011-0320-1]. Journal of Applied Electrochemistry [online], 2011, vol. 41, p. 951-959.
- Zimmermann, Angelo J. O., et al. Os novos aços inoxidáveis EUROFER utilizados em fusão nuclear [doi:10.1590/S0370-44672010000200012]. Religião & Sociedade [online], 2010, vol. 63, p. 287-292.