Disertación de Maestría
DOI
10.11606/D.3.2009.tde-01122009-163937
Documento
Autor
Nombre completo
Angelo José de Oliveira Zimmermann
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Padilha, Angelo Fernando (Presidente)
Plaut, Ronald Lesley
Sandim, Hugo Ricardo Zschommler
Título en portugués
Encruamento e recristalização dos aços inoxidáveis EUROFER e ODS-EUROFER para aplicação em reatores de fusão nuclear.
Palabras clave en portugués
Engenharia metalúrgica
Ensaios da estrutura dos materiais
Materiais nucleares
Resumen en portugués
Este trabalho consiste em uma pesquisa sobre aços inoxidáveis ferríticomartensíticos de ativação reduzida (RAFM): EUROFER (9Cr-1W) e ODS-EUROFER (9Cr-1W-0,3Y2O3), envolvendo o encruamento e a recristalização destas duas ligas com o objetivo de estudar a influência de uma dispersão de partículas nanométricas na recristalização de aços inoxidáveis. O conceito de materiais de ativação reduzida é discutido e é apresentada a aplicação destes aços tanto na estrutura de diversor do ITER quanto na primeira parede no módulo de câmara fértil do reator DEMO. As placas, no estado revenido, foram laminadas a frio em um laminador de pequeno porte. As curvas de encruamento de ambos os materiais mostram um comportamento quase linear. Os tratamentos isócronos de uma hora, entre 300 e 750 °C, resultaram curvas de amolecimento que indicam uma forte resistência à recristalização da liga ODS-EUROFER, em concordância com os modelos teóricos. A liga EUROFER-97 apresentou recristalização muito similar a liga comercial 430, mas com maior dureza inicial, devido a maior quantidade de elementos intersticiais.
Título en inglés
Work hardening and recrystallization of EUROFER and ODS-EUROFER stainless steels to nuclear fusion reactors application.
Palabras clave en inglés
Materials structure testing
Metallurgical engineering
Nuclear materials
Resumen en inglés
This work studies reduced activation ferritic-martensitic (RAFM) stainless steels: EUROFER (9Cr-1W) and ODS-EUROFER (9Cr-1W-0,3Y2O3), and their work hardening and recrystallization behaviour to better understand the influence of a dispersion of nanometric particles on the recrystallization process of stainless steels. The concept of reduced activation materials is discussed and the application of these steel alloys, such as in the divertor structure of ITER (International Thermonuclear Experimental Reactor) and as in the DEMO reactor breeding blanket first wall is shown. The plates, in the as-tempered condition, were cold rolled in a laboratory rolling mill. The work hardness curves of both materials presented an approximately linear behavior with strain increase. One hour isochronal treatments, in the temperature range from 300 to 750 °C, resulted in softening curves that indicated a strong resistance to recrystallization of the alloy ODS-EUROFER, supporting the theorical models. The EUROFER-97 recrystallization showed a similar behaviour to the commercial 430 alloy, however with higher initial hardness, due to the larger amount of interstitial elements.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
zimmermannFicha.pdf (77.14 Kbytes)
Fecha de Publicación
2010-05-24
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • TERADA, Maysa, et al. Corrosion behavior of Eurofer 97 and ODS-Eurofer alloys compared to traditional stainless steels [doi:10.1007/s10800-011-0320-1]. Journal of Applied Electrochemistry [online], 2011, vol. 41, p. 951-959.
  • Zimmermann, Angelo J. O., et al. Os novos aços inoxidáveis EUROFER utilizados em fusão nuclear [doi:10.1590/S0370-44672010000200012]. Religião & Sociedade [online], 2010, vol. 63, p. 287-292.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.