Tesis Doctoral
DOI
10.11606/T.3.2004.tde-19072005-131103
Documento
Autor
Nombre completo
María Cristina Moré Farías
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2004
Director
Tribunal
Tanaka, Deniol Katsuki (Presidente)
Medeiros, João Telésforo Nóbrega de
Pintaúde, Giuseppe
Taqueda, Maria Elena Santos
Tschiptschin, Andre Paulo
Título en portugués
Influência da velocidade de deslizamento, da carga normal e da transformação martensítica induzida por deformação plástica na resistência ao desgaste por deslizamento dos aços inoxidáveis austeníticos.
Palabras clave en portugués
aços inoxidáveis austeníticos
desgaste por deslizamento
planejamento de experimentos
transformação martensítica
Resumen en portugués
Neste trabalho, estudaram-se os mecanismos de desgaste por deslizamento dos aços AISI 304 e AISI 316 em função da carga normal (de 6 N a 20 N) e da velocidade tangencial (de 0,07 m/s a 0,81 m/s). De acordo com o planejamento fatorial 23, realizaram-se ensaios de desgaste em equipamento convencional, do tipo pino-contra-disco. Foram usadas técnicas de análise das superfícies e das partículas após o desgaste: microscopia eletrônica de varredura (MEV), difração de raios-X, espectroscopia Mössbauer, rugosidade, temperatura e dureza instrumentada. Concluiu-se que os mecanismos de desgaste por deslizamento para os aços AISI 304 e AISI 316 são dominados pela deformação plástica (desgaste por oxidação de partículas metálicas, desgaste adesivo e desgaste misto). A variação da taxa de desgaste dos dois materiais dependeu do efeito da interação entre os níveis de carga normal e velocidade tangencial. Por meio do planejamento composto central, foi possível obter um modelo empírico da variação da taxa de desgaste em função da carga normal e da velocidade.
Título en inglés
Influence of sliding velocity, applied load and strain-induced martensitic transformation on the sliding wear resistance of the austenitic stainless steels.
Palabras clave en inglés
austenitic stainless steels
experiments design
martensitic transformation
sliding wear
Resumen en inglés
In this work, sliding wear mechanism of AISI 304 and AISI 316 austenitic stainless steels were studied as a function of the applied load (from 6 N to 20 N) and the tangential velocity (from 0.07 m/s to 0.81 m/s). Following the 23 factorial design, wear experiments were performed using a conventional pin-on-disc machine. Worn surfaces and wear debris analysis techniques were used: scanning electron microscopy (SEM), X-ray diffraction, Mössbauer spectroscopy, stylus profiling, surface temperature measurement and instrumented indentation. Plasticity-dominated wear (metallic debris oxidation, adhesive wear and mixed wear) are the sliding wear mechanisms for AISI 304 and AISI 316 steels. The wear rate behavior depended on interaction effect between applied load and tangential velocity. An empirical model of wear rate as a function of applied load and tangential velocity was obtained by means of the central composite design.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2005-09-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.