Mémoire de Maîtrise
DOI
10.11606/D.25.2011.tde-28072011-095644
Document
Auteur
Nom complet
Yvette Alania Salazar
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2011
Directeur
Jury
Francisconi, Paulo Afonso Silveira (Président)
Borges, Ana Flávia Sanches
Veronezi, Maria Cecilia
Titre en portugais
Resistência de união à microtração entre camadas de materiais restauradores de diferentes matrizes
Mots-clés en portugais
Adesivos dentários
Resina composta
Resumé en portugais
A resina de silorano e a sua polimerização catiônica apresentam diferenças quanto aos materiais a base de metacrilato. Como materiais restauradores, estes poderiam ser utilizados juntos, no entanto suas moléculas diferentes poderiam provocar incompatibilidade. Por isso é importante avaliar a união interfacial desses materiais tendo como objetivo a comparação da resistência de união a microtração entre camadas de Filtek P90 aderidas a Filtek Z350, Filtek P90 ou Vitremer utilizando Adper Single Bond 2 ou o Sistema Adesivo P90. Os substratos dos espécimes a serem testados foram fabricados utilizando uma matriz de silicone (5mm x 5mm x 2.5mm) e fotoativados por 40 segundos (Blue Star 3, Microdont; 1076mW/cm2). De acordo com o grupo testado, foi usada ou não uma camada de adesivo fotoativado por 10 segundos. O segundo substrato (2,5mm) foi aplicado e fotoativado por 40 segundos. Os espécimes foram secionados com formato de palito, com uma área de 0,64mm2, e armazenados em água destilada a 37ºC por 24 horas. Realizou-se o teste de microtração utilizando a máquina de ensaios universal com uma velocidade de 0,5mm/min. Foi analizado o tipo de fratura resultante. Os resultados foram analisados utilizando ANOVA e o teste de Tukey (p<0.05). A média e desvio-padrão dos resultados da resistência de união em MPa são: G1 Pad (P90/adesivo P90/P90) 50.9±15.3, G2 P (P90/sem adesivo/P90) 40.2±10.2, G3 Z (Z350/sem adesivo/Z350) 62.1±15.2, G4 Ppol (P90/sem adesivo, tira de poliéster/P90) 28.8±9.2, G5 ZadP (Z350/adesivo P90/P90) 62.1±8.2, G6 PSBZ (P90/Single Bond 2/Z350) 37.1±12.5, G7 ZSB (Z350/Single Bond 2/Z350) 54.3±12.3, G8 VitrZ (Vitremer/Single Bond 2/Z350) 37.4±7.4 e G9 VitrP (Vitremer/adesivo P90/P90) 34.9±4.1. Diferença significativa foi observada entre os grupos G2 e G3, e G5 e G6. Não foi observada diferencia significativa entre os grupos G8 e G9, G5 e G7, G1 e G6. Dentro das limitações do estudo, pode-se concluir que a resina de silorano demonstrou propriedades de adesão similares quando aderida com resina de metacrilato. Valores significativamente menores foram observados entre camadas de P90 (G2) quando comparados com Z350 (G3).
Titre en anglais
Bond strength between layers of silorane and methacrylate-based materials
Mots-clés en anglais
Composite resins
Dental adhesives
Resumé en anglais
Silorane resin and its cationic polymerization are different from resin-based materials. As restorative materials, their use together could cause some incompatibility that raises the question about the importance of interfacial bonding properties. This study aimed to compare the microtensile bond strengths between layers of Filtek P90 bonded with itself, Filtek Z350 or Vitremer using Adper Single Bond 2 and P90 Adhesive System. Initially, substrates for the testing specimens were fabricated using a silicone mold (5mm x 5mm x 2.5mm) and light-cured for 40 s (Blue Star 3, Microdont; 1076mW/cm2). According to the testing group, it was used or not an adhesive layer, light-cured for 10 s. The second increment (2.5mm) was cured for 40 s. The specimens were sectioned in beams with 0.64mm2 cross-sectional area and stored in distilled water at 37ºC for 24 h. Microtensile bond strength test was performed using a universal testing machine with a 0.5mm/min crosshead speed. Failure modes were assessed. Values were calculated in MPa. Data were analyzed with ANOVA and Tukeys post-hoc tests at a 5% significance level. Microtensile bond strength means and standard deviation are: G1 Pad (P90/P90 adhesive/P90) 50.9±15.3, G2 P (P90/without adhesive/P90) 40.2±10.2, G3 Z (Z350/without adhesive/Z350) 62.1±15.2, G4 Ppol (P90/without adhesive, polyester strip/P90) 28.8±9.2, G5 ZadP (Z350/P90 adhesive/P90) 62.1±8.2, G6 PSBZ (P90/Single Bond 2/Z350) 37.1±12.5, G7 ZSB (Z350/Single Bond 2/Z350) 54.3±12.3, G8 VitrZ (Vitremer/Single Bond 2/Z350) 37.4±7.4 e G9 VitrP (Vitremer/P90 adhesive/P90) 34.9±4.1. Significant difference was showed among G2 and G3, G5 and G6. No significant difference was found between G8 and G9, G5 and G7, G1 and G6. Conclusions: Within the limitations of this study, it can be concluded that silorane composite showed similar bonding properties when bonded with methacrylate-based materials. Significantly lower bond strength was observed between layers of P90 than of Z350.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2011-07-29
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.