Master's Dissertation
DOI
10.11606/D.25.2011.tde-27092011-162138
Document
Author
Full name
Marcela Charantola Rodrigues
Institute/School/College
Knowledge Area
Date of Defense
Published
Bauru, 2011
Supervisor
Committee
Franco, Eduardo Batista (President)
Borges, Ana Flávia Sanches
Nunes, Margareth Calvo Pessutti
Title in Portuguese
Influência da variação da densidade de potência na contração de polimerização e na pigmentação de resinas compostas fotossensíveis
Keywords in Portuguese
Contração
Cor
Polimerização
Abstract in Portuguese
O presente estudo, in vitro, teve como objetivo avaliar a influência da variação da densidade de potência (300, 600, 1000 e 1550 mW/cm2) na contração de polimerização e na pigmentação de duas resinas compostas, Filtek Z250 e Filtek Z350XT (3M/ESPE). Para avaliação das forças geradas durante a contração de polimerização foram utilizadas duas bases de aço, em forma retangular (6 X 2 mm), posicionadas paralelamente na máquina de ensaios (Emic - DL 500), uma conectada à célula de carga de 100 Kg e, a outra, ao braço fixo. As resinas compostas foram introduzidas entre as bases metálicas, com altura de 1mm, volume de 12mm3 e fator C de 1,5. Para fotoativação foi utilizado o aparelho LED Blue Star 3 (Microdont Micro Usinagem de Precisão LTDA), determinando-se o tempo de 20 s para as diferentes densidades de potência. As bases ficaram fixas durante o ensaio (120 s) e as forças geradas durante a polimerização foram registradas numericamente e por meio de gráficos [força (N) x tempo (s)], num total de dez ensaios para cada grupo. Para os testes de pigmentação foram confeccionados, em uma matriz pré-fabricada, cinco espécimes circulares (6 mm X 2 mm) para cada grupo. As avaliações das alterações de cor (_E) foram realizadas com o Espectrofotômetro Easyshade com o sistema CIE-Lab, em diferentes períodos (inicial, após 6 e 12hs, 1, 2, 3, 4 e 5 dias de imersão em café). Os resultados obtidos foram submetidos à análise estatística ANOVA a dois critérios e teste Tukey para comparações individuais (p<0,05). Os resultados evidenciaram que a variação da densidade de potência influenciou diretamente na indução da contração de polimerização, com geração de forças significantemente maiores à medida que se aumentou os valores de irradiância, independente da resina composta utilizada. De forma semelhante, as alterações de cor apresentaram uma relação com a variação da densidade de potência, porém de forma indireta, evidenciando-se que o aumento progressivo da irradiância inferiu em menores valores de _E, assim como uma pigmentação mais acentuada para a resina composta nanoparticulada em relação à resina micro-híbrida. Considerando a observação de efeitos distintos com emprego de diferentes densidades de potência, dentro de um mesmo tempo de fotoativação das resinas compostas analisadas, tanto em relação à indução da contração de polimerização quanto de alteração de cor, deve ser concebido que o fator densidade de potência não pode ser estabelecido de forma independente aos demais parâmetros técnicos relacionados à dose de irradiância, à sequência de energia necessária e ao espectro de luz requerido para efetivação da polimerização das diferentes formulações de compósitos disponíveis.
Title in English
Influence of variation of power density on polymerization shrinkage and pigmentation of photosensitive resins
Keywords in English
Color
Polymerization
Shrinkage
Abstract in English
The aim of this in vitro study was to evaluate the influence of the power density (300, 600, 1000 and 1550 mW/cm2) on polymerization shrinkage and pigmentation of two composite resins, Filtek Z250 and Filtek Z350XT (3M/ESPE). The experimental groups were set based on different combinations of the influencing factors. For the polymerization shrinkage test two steel bases with a parallel disposition were used, the movable one was connected to a 100 kg load cell and the other one was fixed using a universal testing machine (EMIC - DL 500). The resin composite was inserted between the bases and light-cured for 20 s with a LED unit (Blue Star 3, Microdont) The bases stayed fixed during the test (120 s) and the polymerization stresses generated were recorded in graphs [curves force (N) x time (s)]. A total of ten tests for each group were made. For the pigmentation tests five circular specimens (6 mm X 2 mm) for each group were made using a prefabricated mold. Using the color-measuring device Easyshade with the CIE-Lab system, evaluations were made at different times (baseline, after 6 hours, 12 hours, 1, 2, 3, 4 and 5 days of coffee immersion). Statistical analysis was performed with two-way ANOVA and Tukey test for individual comparisons (p <0.05). The results showed that the power density variation directly influenced the induction of polymerization shrinkage, with significantly greater generation force as it increased the values of irradiance, independent of the resin used. Similarly, color changes showed a relation with the power density variation, however demonstrating indirectly that the gradual increase in irradiance inferred at lower values of _E, as pigmentation was more pronounced for the composite with nanoparticles compared to a micro-hybrid resin. Considering the observation of various effects when using different power densities within the same light-curing time of the composite resins analyzed, in relation to the induction of polymerization shrinkage and color change, should be understood that the power density factor can not be established independently of other technical parameters related to the irradiation dosage, the sequence of necessary energy and light spectrum required to effecting the polymerization of composites with different available formulations.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2011-10-03
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.