• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Tese de Doutorado
DOI
10.11606/T.25.2011.tde-09122011-100434
Documento
Autor
Nome completo
Juan Rommel Medina Valdivia
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Bauru, 2011
Orientador
Banca examinadora
Mondelli, Rafael Francisco Lia (Presidente)
Arita, César Augusto
Bonachela, Wellington Cardoso
Carvalho, Renato Savi de
Francischone, Carlos Eduardo
Título em português
Resistência de união entre cimentos resinosos e zircônia
Palavras-chave em português
Cimentos de resina
Resistência ao cisalhamento
Zircônio
Resumo em português
Este estudo avaliou a resistência de união de cimentos resinosos à zircônia tetragonal parcialmente estabilizada com ítrio (NobelProceraTM Zircônia) submetida a tratamentos superficiais mecânicos e químicos. Os cimentos utilizados foram o cimento resinoso auto-condicionante de polimerização química Multilink (Ivoclar Vivadent) associado ao Metal/Zirconia Primer (Ivoclar Vivadent) e o cimento resinoso auto-adesivo de polimerização química e dual RelyX U100 (3M-ESPE) associado ao adesivo Adper Single Bond Plus 2 (3M-ESPE). Utilizando 40 cilindros de zircônia (diâmetro de 3,5 mm) foram realizados 120 ensaios (n=40 para cada cimento). Para cada cimento os cilindros foram divididos em 4 grupos (n=10) em função do tratamento superficial avaliado: 1- sem tratamento; 2- agente de união (primer ou adesivo); 3- jateamento com oxido de alumínio 50µm; 4- associação do jateamento e o agente de união. A aplicação do cimento resinoso foi realizada utilizando uma matriz de teflon com orifício central de 3,5mm de diâmetro por 3,0mm de profundidade. Após a aplicação de cada cimento nas 4 condições de superficie, os espécimes foram armazenados em água deionizada a 37ºC durante 24h e submetidos ao teste de resistência ao cisalhamento. Os resultados foram analisados com ANOVA a dois critérios e teste de Tukey (p<0,05). Sem tratamento superficial o RelyX U100 químico (5,52 Mpa) e dual (6,53 Mpa) tiveram melhor comportamento que o cimento Multilink (0,76). A associação do jateamento e o agente de união melhorou os valores de resistência de união para o cimento Multilink (7,68 Mpa) e para o cimento RelyX U100 dual (10,26 Mpa), sendo este último superior a todos os outros grupos. A associação do Adper Single Bond Plus 2 e o RelyX U100 sem jateamento, deve ser evitado.
Título em inglês
Bond strenght between resin cements and zirconia
Palavras-chave em inglês
Resin cements
Shear bond strength
Zirconium
Resumo em inglês
The aim of this study was to evaluate the shear bond strength of resin cements to the yttria stabilized tetragonal zirconia (NobelProceraTM Zirconia) subjected to mechanical and chemical surface treatments. The cements used were: a self-etching resin cement with chemical polymerization Multilink (Ivoclar - Vivadent) associated to the Metal / Zirconia Primer (Ivoclar - Vivadent) and self-adhesive resin cement with chemical and dual polymerization RelyX U100 (3M-ESPE) associated to the adhesive Single Bond Plus Adper 2 (3M-ESPE). Using 40 cylinders of zirconia (3.5 mm diameter) were performed 120 trials (n = 40 for each cement). For each cement, cylinders were divided into four groups (n = 10) based on the surface treatment rated: 1 - untreated, 2 - bonding agent (primer or adhesive) 3 air abrasion with 50µm aluminum oxide, 4 - combination of air abrasion and bonding agent. The application of resin cement was performed using a teflon matrix with a central hole 3.5 mm in diameter and 3.0 mm deep. After application of each cement in the four surface conditions, the specimens were stored in deionized water at 37 ° C for 24 hours and tested for shear bond strength. Results were analyzed with an ANOVA Two Criteria and Tukey's test (p <0.05). Without surface treatment, chemical RelyX U100 (5.52 MPa) and dual (6.53 MPa) had better behavior than Multilink Cement (0.76). The combination of air abrasion and bonding agent improved the bond strength values for Multilink (7.68 MPa) and for RelyX U100 dual (10.26 MPa), this one superior to all other groups. The association of Adper Single Bond 2 and RelyX U100 Plus without air abrasion, should be contraindicated.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2011-12-09
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2022. Todos os direitos reservados.