Disertación de Maestría
DOI
10.11606/D.25.2013.tde-03092013-160023
Documento
Autor
Nombre completo
Carlos Andrés Villavicencio Espinoza
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2013
Director
Tribunal
Atta, Maria Teresa (Presidente)
Veronezi, Maria Cecilia
Wang, Linda
Título en portugués
Avaliação da interface de adesão à dentina humana de um sistema restaurador adesivo à base de silorano, em cavidades de Classe I, analisados por teste de microtração e microscopia óptica
Palabras clave en portugués
Adesivos dentinários
Resinas compostas
Resistência à tração
Resumen en portugués
Este estudo teve como objetivo a análise da interface de adesão à dentina humana, de um sistema restaurador adesivo à base de silorano. Foram confeccionadas cavidades com 4mm X 3mm X 5mm em 40 molares humanos extraídos divididos em 4 grupos aleatoriamente: Grupos SB e SB-6m: sistema adesivo (Adper™ Single Bond) + resina composta (Filtek Z250); Grupos P90 e P90-6m: sistema adesivo (P90 System Adhesive) + resina composta (Filtek P90™). Em todos os grupos, as restaurações foram inseridas em 4 incrementos oblíquos. Após a restauração, os dentes foram seccionados em fatias de 0,8mm de espessura em uma máquina de cortes com um disco de diamante. Uma fatia de cada dente foi separada aleatoriamente para análise em microscópio óptico para verificação de fendas na interface adesiva. As demais fatias foram seccionadas em palitos (0,8mm X 0,8mm) para os testes de microtração em uma máquina de ensaios universal EMIC. Os e dos grupos SB e P90 permaneceram em água deionizada em estufa a 370C por 24 horas e os grupos SB-6m e P90-6m permaneceram em água deionizada em estufa a 370C por um período de 6 meses. Os resultados de resistência de união foram submetidos à análise de variância a 2 critérios ANOVA e a presença de fendas internas foi analisada pelo testeChi-quadrado. Houve diferença estatisticamente significante na resistência de união entre os materiais (p>0,05) e tempo de armazenagem. Quanto à presença de fendas internas, foi evidenciada sua presença em todos os grupos, sem diferença etatisticamente significante entre eles (p>0,05). Conclui-se que não houve diferença entre os sistemas restauradores á base de Bis-GMA e de silorano os 2 períodos avaliados (24h e 6 meses).
Título en inglés
Evaluation of the interface of a silorane based restorative system to dentin of Class I cavities by microtensile bond strength test and optical microscopy
Palabras clave en inglés
Composite resins
Dentin-Bonding agents
Tensile strength
Resumen en inglés
This study aimed to analyse the adhesive interface to human dentin of a silorane based adhesive system. Cavities were fabricated with 4.0 mm X 3mm X 5mm in 40 extracted human molars randomly divided into 4 groups: Groups SB and SB-6m: adhesive system (Adper™ Single Bond) + composite (Filtek Z250); Groups P90 and P90- 6m: adhesive system (P90 System Adhesive) + composite (Filtek™ P90). In all groups, the restorations were inserted in 4 oblique increments. After 24 hours, teeth were sectioned buccolingually into 0.8mm slices with diamond saw. One slice of each tooth was randomly separated for microscope analysis. The other slices were sectioned into 0.8mm X0.8mm sticks for microtensile tests in a universal testing machine EMIC. Sticks of groups SB and P90 remained in deionized water at 370C C for 24 hours and sticks of groups SB-6m and P90-6m remained in deionized water at 370C for a period of six months. After storage period . The results of bond strength were analysed by Two-way ANOVA and the presence of internal gaps was analyzed by chi-square test. There was no significant difference in bond strength between materials (p> 0.05) and storage time. Regarding the presence of internal rifts, their presence was evident in all groups, with no statistically significant difference between them (p> .05).
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-09-05
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.