Thèse de Doctorat
DOI
10.11606/T.25.2014.tde-16072014-095626
Document
Auteur
Nom complet
Marcela Ferraz Catramby
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2014
Directeur
Jury
Valle, Accacio Lins do (Président)
Almeida, Ana Lúcia Pompéia Fraga de
Compagnoni, Marco Antonio
Elias, Carlos Nelson
Francisconi, Paulo Afonso Silveira
Titre en portugais
Avaliação do comportamento mecânico e da microestrutura de duas marcas comerciais de zircônia monolítica 3Y-TZP sob influência de diferentes parâmetros de sinterização
Mots-clés en portugais
Cerâmica
Materiais Biomédicos e Odontológicos
Resistência de Materiais
Resumé en portugais
Cerâmicas a base de zircônia para coroas e próteses fixas monolíticas prometem suprimir a vulnerabilidade ao lascamento de restaurações de múltiplas camadas, proporcionando estética e resistência mecânica simultâneas. No entanto, é possível que as alterações realizadas para maximizar suas propriedades óticas possam afetar a resistência mecânica. O presente estudo teve por objetivo comparar, com base na microestrutura, o comportamento mecânico de duas marcas comerciais de zircônias monolíticas a uma zircônia convencional para infraestruturas, observando ao mesmo tempo algumas variações nos parâmetros de sinterização. As zircônias monolíticas ceramill Zolid e Prettau e a zircônia convencional IPS e.max ZirCAD foram sinterizadas sob a temperatura preconizada pelos respectivos fabricantes, formando os grupos Z1450, P1600 e I1530. Adicionalmente, foram criados os grupos Z1530 e Z1600, representados pela zircônia ceramill Zolid submetida a ciclos modificados. Foram confeccionados 13 corpos de prova para cada grupo, os quais foram submetidos aos ensaios de difração de raios-x, densidade, análise do tamanho médio de grão e resistência à flexão em 4 pontos. Os espectros de difração revelaram a presença da fase tetragonal metaestável em todos os grupos antes e após a sinterização. Quanto à densidade, apresentou-se superior a 99% apenas nos grupos formados pelas zircônias Prettau e IPS e.max ZirCAD. O tamanho médio dos grãos permaneceu abaixo de 1m em todas as situações, sendo maior para o grupo P1600 (0,814m) e menor para o grupo Z1450 (0,463m). Embora tenha sido observada uma tendência de melhoria nos resultados sob taxa de aquecimento mais lenta, os grupos formados pela zircônia monolíticas ceramill Zolid obtiveram os valores mais baixos de confiabilidade (m=4,58 para Z1530) e de resistência mecânica (621,01±138,08MPa para Z1450). A zircônia Prettau apresentou valores de resistência mecânica mais altos e homogêneos (864,18±118,21MPa), contudo inferiores aos da zircônia convencional (1057,41±150,54MPa). Os resultados revelam que as zircônias monolíticas sob estudo possuem características microestruturais e propriedades mecânicas distintas das observadas para a zircônia convencional.
Titre en anglais
Microstructural and mechanical evaluation of two commercial monolithic 3YTZP zirconia under various sintering conditions
Mots-clés en anglais
Biomedical and Dental Materials
Ceramic
Material Resistance
Resumé en anglais
Monolithic zirconia ceramics for crown and bridge applications were designed to eliminate chipping trends of bilayered restorations, providing both aesthetic and mechanical strength. Nonetheless, it has been suggested that improvements in optical properties may affect the mechanical strength of these materials. The present study aimed to compare, based on a microstructural analysis, the mechanical behavior of two commercial monolithic zirconia ceramics with a conventional core zirconia material, as well as to verify sintering parameters modifications. Two monolithic zirconia ceramics (Ceramill Zolid and Prettau) and a conventional core zirconia material (IPS e.max ZirCAD) were sintered according to manufacturer´s recommendations, forming groups Z1450, P1600 and I1530. Extra groups, Z1530 and Z1600, were originated from ceramill Zolid zirconia specimens subjected to modified sintering cycles. The thirteen specimens that were manufactured for each group were submitted to x-ray diffraction analysis, density, average grain size determination and 4-point-bending tests. X-ray diffraction analysis revealed the presence of tetragonal metastable phase in all groups before and after sintering. Relative density found for Prettau and IPS e.max ZirCAD were greater than 99%. The average grain size remained below 1m for all groups. P1600 showed the largest grain sizes (0,814m) while Z1450 (0,463m) demonstrated the smallest ones. Groups originated from ceramill Zolid also presented the lowest Weibull modulus (m=4,58 for Z1530) and flexural strength results (621,01±138,08MPa for Z1450), regardless of non significant improvements that were achieved when using a low heating rate protocol. Prettau zirconia showed better mechanical behaviour and a more homogeneous distribution of results (864,18±118,21MPa), although lower than those of IPS e.max ZirCAD zirconia (1057,41±150,54MPa). Findings from this study show that the two commercial monolithic zirconia under analysis developed distinct mechanical properties and microstructural features from data established for conventional zirconia.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2014-07-16
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.