Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.25.2022.tde-11112022-120208
Document
Auteur
Nom complet
Pedro Rodrigues Minim
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2022
Directeur
Jury
Rubo, Jose Henrique (Président)
Borges, Ana Flávia Sanches
Fortulan, Carlos Alberto
Lisboa Filho, Paulo Noronha
Titre en portugais
Efeitos dos parâmetros de sinterização e da adição de aglutinantes nas características estruturais de biocerâmicas densas de hidroxiapatita bovina
Mots-clés en portugais
Cerâmica
Durapatita
Materiais biocompatíveis
Resumé en portugais
A hidroxiapatita (HA) proveniente de estrutura óssea bovina tem elevada importância dentre os biomateriais devido à sua biocompatibilidade e bioatividade. Entretanto, as cerâmicas densas de hidroxiapatita bovina apresentam propriedades mecânicas insuficientes para a confecção de infra-estuturas de prótese fixa. O presente estudo objetivou avaliar o efeito da adição de polivinilbutiral (PVB) e ácido esteárico (AE) e de duas metodologias de sinterização (2-step e convencional), nas propriedades mecânicas de biocerâmica densa policristalina de HA de origem bovina. Dessa forma, a partir de um esquema fatorial 2x2, 4 grupos foram avaliados. Para tanto, a HA foi extraída de ossos bovinos, calcinados a 900 °C, nanoparticuladas em moinho de bolas e submetida à prensagem uniaxial estática em discos, conforme a norma ISO 6872. Os grupos submetidos a sinterização convencional (HAAC e HASC) tiveram pico máximo de temperatura de 1300 °C e resfriamento lento até a temperatura ambiente. Já os grupos com sinterização 2-step (HAA2 e HAS2), tiveram pico máximo de 950 °C com resfriamento rápido para 880 °C e posterior resfriamento lento a temperatura ambiente. As amostras dos 4 grupos foram caracterizadas por difratometria de raios-x (DRX), análise térmica diferencial (DTA) e espectroscopia de infravermelho por transformada de Fourrier (FTIR), e avaliadas pelos testes de microscopia eletrônica de varredura (MEV) densidade relativa, através do princípio de Arquimedes, pelo teste de resistência à flexão biaxial e pela análise do módulo de elasticidade. Os valores obtidos de densidade relativa e resistência à flexão foram submetidos ao teste de normalidade de Shapiro-Wilk e a partir disso foi realizado teste de Kruskal-Wallis e pós teste de Dunn, para todos os testes. Foi possível concluir que as cerâmicas de HA submetidas a sinterização convencional e sem a adição de aglutinantes obteve melhores propriedades mecânicas que os demais grupos.
Titre en anglais
Effects of the sintering parameters and the addition of agglutinants on the structural characteristics of bovine hydroxyapatite dense bioceramics
Mots-clés en anglais
Biocompatible materials
Ceramics
Durapatite
Resumé en anglais
Hydroxyapatite (HA) from bovine bone structure has high importance among biomaterials due to its biocompatibility and bioactivity. However, hydroxyapatite dense ceramics have inadequate mechanical properties for their intended purpose. The present study aimed to evaluate the effect of the addition of polyvinyl butyral (PVB) and stearic acid (SA) and two sintering methodologies (2-step and conventional) on the mechanical properties of bovine hydroxyapatite dense polycrystalline bioceramic. Thus, from a 2x2 factorial scheme, 4 groups were evaluated. Therefore, HA was extracted from bovine bones, turned into nanoparticles in a ball mill and subjected to uniaxial and isostatic pressing into discs, according to the ISO 6872 standard. The groups submitted to conventional sintering (HAAC and HASC) had a maximum temperature peak of 1300 °C and slow cooling to room temperature. The groups with 2-step sintering (HAA2 and HAS2) had a maximum peak of 950 °C with rapid cooling to 880 °C and subsequent slow cooling to room temperature. The samples of the 4 groups were characterized by x-ray diffractometry (XRD), differential thermal analysis (DTA) and Fourrier transform infrared spectroscopy (FTIR), and evaluated by scanning electron microscopy (SEM) relative density, through the Archimedes principle, by the biaxial flexural strength test and by the analysis of the modulus of elasticity. The values obtained for relative density and flexural strength were submitted to the Shapiro-Wilk normality test and from there, the Kruskal-Wallis test and Dunn's post-test were performed for all tests. It was possible to conclude that the HA ceramics submitted to conventional sintering and without the addition of binders obtained better mechanical properties than the other groups.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2022-12-14
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.