Disertación de Maestría
DOI
https://doi.org/10.11606/D.25.2022.tde-10112022-154047
Documento
Autor
Nombre completo
Letícia Florindo Pereira
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2022
Director
Tribunal
Borges, Ana Flávia Sanches (Presidente)
Cesar, Paulo Francisco
Goulart, Celso Antonio
Soares, Simone
 
Título en portugués
Cerâmica experimental a base de fosfato de cálcio com adição de nanopartículas de dióxido de titânio: desenvolvimento, caracterização e análise de propriedades mecânicas e química
Palabras clave en portugués
Apatitas
Cerâmicas
Materiais dentários
Nanotecnologia
Osso
Resumen en portugués
Este estudo propôs o desenvolvimento e caracterização de uma nova cerâmica para uso odontológico feita a partir de hidroxiapatita (HA). A HA foi extraída de ossos bovinos, com a intenção de reaproveitar esses resíduos sólidos e transformá-los em um material sustentável e de baixo custo. Além disso, a adição de nanopartículas de dióxido de titânio (TiO2) (5 e 8%) a este material foi realizada na tentativa de melhorar suas propriedades mecânicas e químicas. Discos (Ø 14 ± 2 mm; espessura = 1.2 ± 0.2 mm) foram obtidos por prensagem uniaxial e isostática a partir de um pó de hidroxiapatita bovina e nanopartículas de TiO2 e sinterizados a 1300ºC por 2 horas. Três grupos experimentais foram desenvolvidos (HA, HA+5%TiO2 e HA+8%TiO2) e caracterizados microestruturalmente por difração de raios-X (DRX), microscopia eletrônica de varredura (MEV) e espectroscopia por energia dispersiva (EDS). Para análise mecânica e química dos materiais, os testes de tenacidade à fratura pelo método da indentação, de resistência à flexão biaxial (RFB) e de solubilidade química foram realizados. Os espectros de DRX revelaram, para o grupo HA, o aparecimento de um pico correspondente ao beta-tricálcio fosfato (ß-TCP). Para HA+5%TiO2 e HA+8%TiO2, toda a composição de HA e TiO2 foi convertida em ß-TCP e titanato de cálcio (CaTiO3). A tenacidade à fratura foi maior para HA+5%TiO2 (1,34 ± 0,26 MPa.m1/2) e HA+8%TiO2 (1,28 ± 0,21 MPa.m1/2) do que para HA (0,65 ± 0,10 MPa.m1/2). HA apresentou resistência característica significativamente maior (295,8 MPa) em relação aos grupos com 5% (235,1 MPa) e 8% (214,4 MPa) de nanopartículas de TiO2. Os valores de módulo Weibull dos três grupos foram estatisticamente semelhantes. Os resultados de solubilidade indicaram que todas as cerâmicas experimentais estavam acima do limite de 2000 ug/cm2 permitido pela International Organization for Standardization (ISO) 6872:2015. A cerâmica experimental de fosfato de cálcio com adições de 5% e 8% de TiO2 alcançou propriedades mecânicas desejáveis, mas valores de solubilidade química muito elevados.
 
Título en inglés
Experimental calcium phosphate ceramic with titanium dioxide nanoparticles: manufacturing, characterization, mechanical and chemical properties analysis.
Palabras clave en inglés
Apatites
Bone
Ceramics
Dental materials
Nanotechnology
Resumen en inglés
The following study proposed the development and characterization of a new ceramic for dental use made from hydroxyapatite (HA) extracted from bovine bones, with the intention of reusing these solid wastes and turning them into a sustainable and low-cost material. Furthermore, the addition of titanium dioxide (TiO2) nanoparticles to this material was carried out in an attempt to improve its mechanical and chemical properties. Disks (Ø = 14 ± 2 mm; thickness = 1.2 ± 0.2 mm) were obtained through uniaxial and isostatic pressing from bovine hydroxyapatite powder and TiO2 nanoparticles and sintered at 1300ºC for 2 hours. Three experimental groups were developed (HA, HA+5%TiO2 and HA+8%TiO2) and microstructurally characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). For mechanical and chemical analysis, indentation fracture (IF), biaxial flexural strength (BFS) and chemical solubility tests were performed. XRD spectra revealed the appearance of a peak corresponding to btricalcium phosphate (ß-TCP) for HA group. For HA+5%TiO2 and HA+8%TiO2, the entire composition was converted into ß-TCP and calcium titanate (CaTiO3). IF toughness was higher for HA+5%TiO2 (1.34 ± 0.26 MPa.m1/2) and HA+8%TiO2 (1.28 ± 0.21 MPa.m1/2) than for HA (0.65 ± 0.10 MPa.m1/2). HA showed significantly higher characteristic stress (295.8 MPa) in relation to groups with 5% (235.1 MPa) and 8% (214.4 MPa) TiO2 nanoparticles. The Weibull modulus values of the three groups were statistically similar. The solubility results indicated that all experimental ceramics were above the 2000 ug/cm2 limit set by the International Organization for Standardization (ISO) 6872:2015. The experimental calcium phosphate ceramic with additions of 5% and 8% of TiO2 achieved desirable mechanical properties, but very high chemical solubility values.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2022-11-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores.
CeTI-SC/STI
© 2001-2024. Biblioteca Digital de Tesis y Disertaciones de la USP.